Certificates
PA612 153HSL-NC010 DUPONT USA
Zytel®
Engineering accessories、Automotive Applications
Mineral reinforcement、Thermal stability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/153HSL-NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak |
| film | Test Condition | Test Method | DUPONT USA/153HSL-NC010 |
|---|---|---|---|
| Tensile strain | Yield，MD | ISO 527-3 | 4.4 % |
| Electrical performance | Test Condition | Test Method | DUPONT USA/153HSL-NC010 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| dielectric strength | IEC 60243-1 | 30 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.60 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.014 |
| relative permittivity | 1MHz | IEC 60250 | 3.20 |
| Surface Resistivity | IEC 60093 | -- ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.016 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/153HSL-NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2400 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 30 % | |
| Flexural modulus | ISO 178 | 2100 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 4.4 % |
| wear resistance | ISO 4649 | 6.00 mm³ | |
| tensile strength | 屈服 | ISO 527-2 | 62.0 Mpa |
| flammability | Test Condition | Test Method | DUPONT USA/153HSL-NC010 |
|---|---|---|---|
| UL flame retardant rating | 0.9mm | IEC 60695-11-10,-20 | HB |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | B | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 27 % | |
| UL flame retardant rating | 0.9mm | UL 94 | HB |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| physical property | Test Condition | Test Method | DUPONT USA/153HSL-NC010 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.4 % |
| MD | ISO 294-4 | 1.3 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 3.0 % |
| viscosity number | 96%H2SO4 | ISO 307 | 115 cm³/g |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.3 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/153HSL-NC010 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：55to160°C | ISO 11359-2 | 1.7E-04 cm/cm/°C |
| TD：-- | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| melting temperature | ISO 11357-3 | 218 °C | |
| Linear coefficient of thermal expansion | MD：-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| TD：-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| MD：-- | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| TD：55to160°C | ISO 11359-2 | 1.8E-04 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 135 °C |
| vicat | ISO 306/B50 | 180 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 62.0 °C |
| Linear coefficient of thermal expansion | TD：EffectiveThermalDiffusivity | ISO 11359-2 | 7E-08 m²/s |