Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS XCY620-100 SABIC INNOVATIVE THAILAND
CYCOLOY™
Electrical applications、Home appliance components
High temperature resistan、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/XCY620-100 |
|---|---|---|---|
| Dart impact equipped with measuring instruments | -30°C,TotalEnergy | ASTMD3763 | 70.0 J |
| 23°C,TotalEnergy | ASTMD3763 | 56.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/XCY620-100 |
|---|---|---|---|
| Tensile stress | 屈服 | ISO527-2/50 | 54.0 Mpa |
| Bending strength 5,6 | ISO178 | 83.0 Mpa | |
| elongation | 断裂 | ASTMD638 | 120 % |
| Tensile strain | 屈服 | ISO527-2/50 | 4.5 % |
| Tensile modulus | ASTMD638 | 2300 Mpa | |
| Tensile stress | 断裂 | ISO527-2/50 | 51.0 Mpa |
| elongation | 屈服 | ASTMD638 | 4.7 % |
| Tensile modulus | ISO527-2/1 | 2200 Mpa | |
| tensile strength | 屈服 | ASTMD638 | 55.0 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTMD790 | 89.0 Mpa |
| tensile strength | 断裂 | ASTMD638 | 52.0 Mpa |
| Tensile strain | 断裂 | ISO527-2/50 | 120 % |
| Flexural modulus | ISO178 | 2200 Mpa | |
| 50.0mm跨距 | ASTMD790 | 2300 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/XCY620-100 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| dielectric strength | 3.20mm,在油中 | IEC60243-1 | 17 KV/mm |
| Volume resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| dielectric strength | 1.60mm,在油中 | IEC60243-1 | 25 KV/mm |
| 0.800mm,在油中 | IEC60243-1 | 35 KV/mm |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/XCY620-100 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| MeltViscosity | 260°C,1500sec^-1 | ISO11443 | 195 Pa·s |
| Water absorption rate | 饱和,23°C | ISO62 | 0.40 % |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.50to0.70 % |
| Melt volume flow rate | 260°C/5.0kg | ISO1133 | 18.0 cm3/10min |
| melt mass-flow rate | 260°C/5.0kg | ASTMD1238 | 22 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/XCY620-100 |
|---|---|---|---|
| vicat | ASTMD152512 | 127 °C | |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 107 °C | |
| Hot deformation temperature 11 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 105 °C |
| MD：-40到40°C | ISO11359-2 | 7E-05 cm/cm/°C | |
| TD：-40到40°C | ISO11359-2 | 7E-05 cm/cm/°C | |
| BallPressure Test | 75°C | IEC60695-10-2 | Pass |
| MD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C | |
| Hot deformation temperature 11 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 126 °C |
| vicat | -- | ISO306/B50 | 127 °C |
| -- | ISO306/B120 | 129 °C | |
| thermal conductivity | ISO8302 | 0.20 W/m/K | |
| TD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |