mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL4412-7G1A1794
bending strength		ISO 178	90.0 Mpa
elongation	Break	ASTM D638	20 %
Tensile strain	Break	ISO 527-2/5	13 %
Bending modulus	50.0mmSpan	ASTM D790	3200 Mpa
Tensile modulus		ISO 527-2/1	3300 Mpa
Tensile modulus			ASTM D638	3300 Mpa
tensile strength	Break	ISO 527-2/5	43.0 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	95.0 Mpa
tensile strength	Break	ASTM D638	44.0 Mpa
		Yield	ASTM D638	53.0 Mpa
		Yield	ISO 527-2/5	55.0 Mpa
Bending modulus		ISO 178	3300 Mpa
elongation	Yield	ASTM D638	4.5 %
Tensile strain	Yield	ISO 527-2/5	4.5 %
thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL4412-7G1A1794
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	134 °C
Hot deformation temperature		1.8MPa,Unannealed,3.20mm	ASTM D648	135 °C
Vicat softening temperature	--	ISO 306/B50	144 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	4.1E-05 cm/cm/°C
		MD：-40to40°C	ASTME831	4.1E-05 cm/cm/°C
		TD：-40to40°C	ASTME831	6.9E-05 cm/cm/°C
Ball Pressure Test	75°C	IEC 60695-10-2	Pass
Vicat softening temperature		ASTM D152510	145 °C
Vicat softening temperature		--	ISO 306/B120	146 °C
Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	6.9E-05 cm/cm/°C
impact performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL4412-7G1A1794
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	15 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	25 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	NoBreak
Charpy Notched Impact Strength	23°C	ISO 179/1eA	25 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	40.0 J
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength		23°C	ISO 180/1U	NoBreak
Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL4412-7G1A1794
Dissipation factor	1MHz	ASTM D150	8.6E-03
Surface resistivity		ASTM D257	2.9E+17 ohms
Dissipation factor	1.90GHz	Internal Method	5.8E-03
Dielectric constant	1.90GHz	Internal Method	2.95
Volume resistivity		ASTM D257	1.8E+17 ohms·cm
Dielectric strength	1.60mm,inOil	ASTM D149	32 KV/mm
Dielectric constant	1MHz	ASTM D150	3.04
Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL4412-7G1A1794
melt mass-flow rate	300°C/1.2kg	ASTM D1238	11 g/10min
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.46 %
Shrinkage rate	MD：3.20mm	Internal Method	0.20-0.60 %
Water absorption rate	Saturation,23°C	ISO 62	0.12 %
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	10.3 cm3/10min