Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL4412-7G1A1794 SABIC INNOVATIVE NANSHA
LEXAN™
Plastic bag
Glass fiber reinforced、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL4412-7G1A1794 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 25 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 40.0 J |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 15 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 25 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL4412-7G1A1794 |
|---|---|---|---|
| dielectric constant | 1.90GHz | 内部方法 | 2.95 |
| dielectric strength | 1.60mm,inOil | ASTM D149 | 32 KV/mm |
| Volume resistivity | ASTM D257 | 1.8E+17 ohms·cm | |
| Surface Resistivity | ASTM D257 | 2.9E+17 ohms | |
| Dissipation Factor | 1MHz | ASTM D150 | 8.6E-03 |
| 1.90GHz | 内部方法 | 5.8E-03 | |
| dielectric constant | 1MHz | ASTM D150 | 3.04 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL4412-7G1A1794 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3300 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 43.0 Mpa |
| elongation | 屈服 | ASTM D638 | 4.5 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 4.5 % |
| tensile strength | 断裂 | ASTM D638 | 44.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 3200 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 55.0 Mpa |
| Tensile modulus | ASTM D638 | 3300 Mpa | |
| elongation | 断裂 | ASTM D638 | 20 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 95.0 Mpa |
| ISO 178 | 90.0 Mpa | ||
| Flexural modulus | ISO 178 | 3300 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 13 % |
| tensile strength | 屈服 | ASTM D638 | 53.0 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL4412-7G1A1794 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20-0.60 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 10.3 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.46 % |
| 饱和,23°C | ISO 62 | 0.12 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 11 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL4412-7G1A1794 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 146 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 6.9E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 6.9E-05 cm/cm/°C | |
| ball-indentation hardness | 75°C | IEC 60695-10-2 | Pass |
| vicat | -- | ISO 306/B50 | 144 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 4.1E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 4.1E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 134 °C |
| vicat | ASTM D152510 | 145 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 135 °C |