Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 73G30HSL DUPONT USA
Zytel® 
Electronic and electrical、Automotive Applications
Thermal stability、Filler: Glass fiber reinf、30% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodDUPONT USA/73G30HSL
Charpy Notched Impact Strength23°CISO 179/1eA16 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U80 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA10 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A10 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU100 kJ/m²
Multi axis Instrumented Impact Energy23°CISO 6603-23.50 J
Impact strength of cantilever beam gap23°CISO 180/1A15 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU80 kJ/m²
Supplementary InformationTest ConditionTest MethodDUPONT USA/73G30HSL
OdorVDA2703.50
Emissions of Organic CompoundsVDA2778.50 µgC/g
hardnessTest ConditionTest MethodDUPONT USA/73G30HSL
ball-indentation hardnessH961/30ISO 2039-1230 Mpa
Rockwell hardnessR级ISO 2039-2121
Mechanical propertiesTest ConditionTest MethodDUPONT USA/73G30HSL
Tensile modulusISO 527-29500 Mpa
Tensile creep modulus1hrISO 899-1-- Mpa
bending strengthISO 178280 Mpa
Flexural modulusISO 1788500 Mpa
Tensile strain断裂ISO 527-23.5 %
Tensile creep modulus1000hrISO 899-1-- Mpa
tensile strength 断裂ISO 527-2190 Mpa
flammabilityTest ConditionTest MethodDUPONT USA/73G30HSL
UL flame retardant rating0.75mmUL 94HB
0.75mmIEC 60695-11-10,-20HB
1.5mmIEC 60695-11-10,-20HB
FMVSS flammabilityFMVSS302B
atomizationF-value(refraction)ISO 645295 %
G-value(condensate)ISO 64521E-04 g
UL flame retardant rating1.5mmUL 94HB
Limiting Oxygen IndexISO 4589-221 %
burning rate1.00mmISO 379550 mm/min
physical property Test ConditionTest MethodDUPONT USA/73G30HSL
Shrinkage rateTDISO 294-40.60 %
MDISO 294-40.20 %
Water absorption rate饱和,23°C,2.00mmISO 626.3 %
MediumDensity1.20 g/cm³
Melt volume flow rate250°C/5.0kgISO 113315.0 cm3/10min
densityISO 11831.36 g/cm³
SpecificHeatCapacity of Melt2280 J/kg/°C
ThermalConductivityofMelt0.26 W/m/K
Water absorption rate平衡,23°C,2.00mm,50%RHISO 621.9 %
Thermal performanceTest ConditionTest MethodDUPONT USA/73G30HSL
melting temperatureISO 11357-3221 °C
Effective thermal diffusivity coefficient9.1E-08 m²/s
Heat distortion temperature0.45MPa,未退火,HDTISO 75-2/B220 °C
vicatISO 306/B50215 °C
Heat distortion temperature1.8MPa,未退火,HDTISO 75-2/A210 °C
Linear coefficient of thermal expansionMDISO 11359-22.6E-05 cm/cm/°C
TDISO 11359-27.5E-05 cm/cm/°C
Glass Transition TemperatureISO 11357-260.0 °C