PA6 Nycast Nyloil Cast Nylons Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Cast Nylons Ltd./Nycast Nyloil |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 75to96 J/m | |
| ASTM D1822 | 69.4to75.7 kJ/m² |
| hardness | Test Condition | Test Method | Cast Nylons Ltd./Nycast Nyloil |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 100to115 |
| Mechanical properties | Test Condition | Test Method | Cast Nylons Ltd./Nycast Nyloil |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 45to55 % |
| tensile strength | ASTM D638 | 65.5to75.8 MPa | |
| Heat distortion temperature | HDT | ASTM D621 | 0.700to0.800 % |
| compressive strength | 10%应变 | ASTM D695 | 82.7to96.5 MPa |
| Tensile modulus | ASTM D638 | 2590to3280 MPa | |
| Flexural modulus | ASTM D790 | 2590to3280 MPa | |
| Compression Modulus | ASTM D695 | 1900to2590 MPa | |
| coefficient of friction | 与自身-动态 | ASTM D1894 | 0.12 |
| Wear factor | K值 | 4.00 | |
| bending strength | ASTM D790 | 96.5to110 MPa | |
| shear strength | ASTM D732 | 55.2to62.1 MPa |
| physical property | Test Condition | Test Method | Cast Nylons Ltd./Nycast Nyloil |
|---|---|---|---|
| Water absorption rate | 饱和 | ASTM D570 | 2.0to2.5 % |
| 24hr | ASTM D570 | 0.50to0.60 % | |
| PVLimit-Unlubed2 | ASTM D570 | 110 MPa | |
| density | ASTM D792 | 1.14to1.15 g/cm³ |
| Thermal performance | Test Condition | Test Method | Cast Nylons Ltd./Nycast Nyloil |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 93.3to204 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 204to221 °C | |
| Continuous use temperature | ASTM D794 | 110 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 9E-05 cm/cm/°C |
| melting temperature | 227to238 °C | ||
| Usage temperature | 间歇 | 166 °C |