PA66 A3HG6 BASF GERMANY
Ultramid®
Automotive sector
Glass fiber reinforced,Oil resistant,Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | BASF GERMANY/A3HG6 |
|---|---|---|---|
| melting temperature | 275 ℃（℉） | ||
| Heat Deflection Temperature | 1.8Mpa，HDT | ISO 75-1/-2 | 250 ℃ |
| melting temperature | ISO 1133 | 275 ℃ | |
| Heat Deflection Temperature | 0.45Mpa，HDT | ISO 75-1/-2 | 250 ℃ |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/A3HG6 |
|---|---|---|---|
| volume resistivity | ASTM D257/IEC 60093 | 1E13 Ω.cm | |
| dielectric constant | 1MHz | IEC 60250 | |
| volume resistivity | IEC 60093 | 1E+13 Ohm.m |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/A3HG6 |
|---|---|---|---|
| Tensile modulus | ISO 527-1/2 | 10000 MPa | |
| ASTM D638/ISO 527 | 10000 kg/cm²(MPa)[Lb/in²] | ||
| flexural modulus | ASTM D790/ISO 178 | 8700 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 275 kg·cm/cm(J/M)ft·lb/in | |
| fracture strain | ISO 527-1/2 | 3.2 % | |
| Breaking stress | ISO 527-1/2 | 190 MPa | |
| bending strength | ISO 178 | 275 MPa |
| other | Test Condition | Test Method | BASF GERMANY/A3HG6 |
|---|---|---|---|
| characteristic | 纤维.增强。 |
| Physical properties | Test Condition | Test Method | BASF GERMANY/A3HG6 |
|---|---|---|---|
| Water absorption rate | 23℃,50%相对湿度 | ISO 62 | 1.5-1.9 % |
| shrinkage rate | ASTM D955 | 0.55 % | |
| density | ASTM D792/ISO 1183 | 1.37 | |
| Water absorption rate | ASTM D570/ISO 62 | 1.5-1.9 % |