POM K500HS KOLON KOREA
KOCETAL®
Thin walled components
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | KOLON KOREA/K500HS |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 82 |
| M级 | ISO 2039-2 | 96 |
| Mechanical properties | Test Condition | Test Method | KOLON KOREA/K500HS |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 30 % |
| bending strength | 23°C | ISO 178 | 95.0 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 67.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2950 Mpa |
| bending strength | 23°C | ASTM D790 | 98.0 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 2900 Mpa |
| tensile strength | 23°C | ASTM D638 | 66.0 Mpa |
| elongation | 断裂,23°C | ASTM D638 | 55 % |
| Electrical performance | Test Condition | Test Method | KOLON KOREA/K500HS |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+14 ohms·cm | |
| dielectric strength | IEC 60243-1 | 19 KV/mm | |
| Surface Resistivity | ASTM D257 | 1E+16 ohms | |
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| Dissipation Factor | 1MHz | ASTM D150 | 6E-03 |
| dielectric strength | ASTM D149 | 19 KV/mm | |
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| dielectric constant | ASTM D150 | 3.70 |
| flammability | Test Condition | Test Method | KOLON KOREA/K500HS |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | KOLON KOREA/K500HS |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 2.0 % |
| TD | ISO 294-4 | 2.2 % | |
| MD | ISO 294-4 | 2.3 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.53 % |
| 平衡,23°C,60%RH | ASTM D570 | 0.22 % | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 14 g/10min |
| 190°C/2.16kg | ISO 1133 | 15 g/10min |
| Thermal performance | Test Condition | Test Method | KOLON KOREA/K500HS |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648A | 110 °C |
| vicat | ASTM D1525 | 162 °C | |
| melting temperature | ISO 11357-3 | 173 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648A | 158 °C |
| melting temperature | ASTM D1525 | 173 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 100 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 1.3E-05 cm/cm/°C |