Certificates
PPS A390M60 TORAY JAPAN
Torelina®
Electronic and Electrical Applications,Electrical appliances
Dimensional stability,Filler: Glass mineral,65% filler by weight,65% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/A390M60 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 17 kJ/m² |
| hardness | Test Condition | Test Method | TORAY JAPAN/A390M60 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 122 |
| Supplementary Information | Test Condition | Test Method | TORAY JAPAN/A390M60 |
|---|---|---|---|
| BarFlowLength | 320°C,1.00mm | 内部方法 | 8.00 CM |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/A390M60 |
|---|---|---|---|
| shear strength | 23°C | JISK7214 | 60.0 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 0.90 % |
| bending strength | 23°C | ISO 178 | 210 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 105 Mpa |
| Flexural modulus | 23°C | ISO 178 | 19500 Mpa |
| coefficient of friction | 0.30 | ||
| Taber abraser | 1000Cycles | ISO 9352 | 70.0 mg |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/A390M60 |
|---|---|---|---|
| dielectric constant | 23°C,1MHz | IEC 60250 | 5.30 |
| dielectric strength | IEC 60243-1 | 21 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 2E-03 |
| flammability | Test Condition | Test Method | TORAY JAPAN/A390M60 |
|---|---|---|---|
| UL flame retardant rating | 0.72mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TORAY JAPAN/A390M60 |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.99 g/cm³ |
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 0.50 % |
| MD:3.00mm4 | 内部方法 | 0.25 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.020 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/A390M60 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 278 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 260 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.9E-05 cm/cm/°C |
| TD | ISO 11359-2 | 2.5E-05 cm/cm/°C |