Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL1414-WH9E195 SABIC INNOVATIVE KOREA
LEXAN™
currency、Electrical field、Electronic field
Processability、Moderate liquidity、Ductility、copolymer、Good demolding performanc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE KOREA/EXL1414-WH9E195 |
|---|---|---|---|
| The impact strength of a simply supported beam without a notch is 7 | 23°C | ISO 179/1eU | 无断裂 |
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 70.0 J |
| Impact strength of simply supported beam gap 7 | -30°C | ISO 179/1eA | 65 kJ/m² |
| Unscented Izod Impact Strength 8 | -30°C | ISO 180/1U | 无断裂 |
| The impact strength of a simply supported beam without a notch is 7 | -30°C | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam gap 7 | 23°C | ISO 179/1eA | 70 kJ/m² |
| Unscented Izod Impact Strength 8 | 23°C | ISO 180/1U | 无断裂 |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE KOREA/EXL1414-WH9E195 |
|---|---|---|---|
| Rockwell hardness | L 计秤 | ASTM D785 | 89 |
| R 级 | ASTM D785 | 121 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE KOREA/EXL1414-WH9E195 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 57.0 Mpa |
| Bending stress | -- 5, 6 | ISO 178 | 85.0 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 120 % |
| Flexural modulus | -- 5 | ISO 178 | 2250 Mpa |
| elongation | 屈服 3 | ASTM D638 | 6.0 % |
| Bending stress | 屈服, 50.0 mm 跨距 4 | ASTM D790 | 92.0 Mpa |
| Tensile modulus | -- 2 | ASTM D638 | 2020 Mpa |
| tensile strength | 屈服 3 | ASTM D638 | 55.0 Mpa |
| 断裂 | ISO 527-2/50 | 60.0 Mpa | |
| elongation | 屈服 | ISO 527-2/50 | 6.0 % |
| Flexural modulus | 50.0 mm 跨距 4 | ASTM D790 | 2230 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2150 Mpa |
| elongation | 断裂 3 | ASTM D638 | 98 % |
| tensile strength | 断裂 3 | ASTM D638 | 50.0 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE KOREA/EXL1414-WH9E195 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | > 1.0E+15 ohms·cm | |
| Dissipation Factor | 100 Hz | ASTM D150 | 1.2E-3 |
| dielectric constant | 100 Hz | ASTM D150 | 2.68 |
| Surface Resistivity | ASTM D257 | > 1.0E+15 ohms | |
| dielectric strength | 0.800 mm, in Oil | ASTM D149 | 16 KV/mm |
| dielectric constant | 1 MHz | ASTM D150 | 2.64 |
| Dissipation Factor | 1 MHz | ASTM D150 | 9.3E-3 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE KOREA/EXL1414-WH9E195 |
|---|---|---|---|
| Hot filament ignition temperature | 3.0 mm | IEC 60695-2-13 | 875 °C |
| Burning wire flammability index | 0.8 mm | IEC 60695-2-12 | 850 °C |
| UL flame retardant rating | 0.40 mm | UL 94 | HB |
| Hot filament ignition temperature | 1.0 mm | IEC 60695-2-13 | 875 °C |
| Burning wire flammability index | 1.0 mm | IEC 60695-2-12 | 960 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE KOREA/EXL1414-WH9E195 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.15 % |
| Shrinkage rate | 横向流动 : 3.20 mm | 内部方法 | 0.40 到 0.80 % |
| Molten Volume Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 9.00 cm3/10min |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 10 g/10 min |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.40 到 0.80 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.35 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE KOREA/EXL1414-WH9E195 |
|---|---|---|---|
| 流动 : 23 到 80°C | ISO 11359-2 | 7.2E-5 cm/cm/°C | |
| 流动 : -40 到 40°C | ASTM E831 | 7.0E-5 cm/cm/°C | |
| Thermal deformation temperature under load | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 139 °C |
| RTI | UL 746 | 125 °C | |
| Thermal deformation temperature under load | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 9 | ISO 75-2/Be | 140 °C |
| vicat | -- | ISO 306/B120 | 146 °C |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 9 | ISO 75-2/Ae | 128 °C |
| 横向 : 23 到 80°C | ISO 11359-2 | 7.2E-5 cm/cm/°C | |
| 横向 : -40 到 40°C | ASTM E831 | 7.5E-5 cm/cm/°C | |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 124 °C |
| Ball Pressure Test | 123 到 127°C | IEC 60695-10-2 | 通过 |
| RTI Imp | UL 746 | 120 °C | |
| vicat | -- | ASTM D152510, ISO 306/B5010 | 145 °C |
| RTI Elec | UL 746 | 130 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE KOREA/EXL1414-WH9E195 |
|---|---|---|---|
| Processing (melt) temperature | 295 到 315 °C | ||
| drying temperature | 120 °C | ||
| Exhaust hole depth | 0.025 到 0.076 mm | ||
| Temperature at the front of the material cylinder | 295 到 315 °C | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 280 到 305 °C | ||
| Temperature | 70 到 95 °C | ||
| screw speed | 40 到 70 rpm | ||
| Temperature at the rear of the barrel | 270 到 295 °C | ||
| Back pressure | 0.300 到 0.700 Mpa | ||
| drying time | 3.0 到 4.0 hr | ||
| Suggested injection volume | 40 到 60 % | ||
| Spray nozzle temperature | 290 到 310 °C |