PPA UF-1007 BK SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Automotive components
High temperature resistan、Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/UF-1007 BK |
|---|---|---|---|
| bending strength | 屈服，2mm/min，23°C | ISO 178 | 279 Mpa |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 11.0 kJ/m² |
| Flexural modulus | 2mm/min，23°C | ISO 178 | 9600 Mpa |
| Tensile modulus | 1mm/min，23°C | ISO 527-2 | 12100 Mpa |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 45.0 kJ/m² |
| tensile strength | 5mm/min，23°C | ISO 527-2 | 194 Mpa |
| elongation at break | 5mm/min，23°C | ISO 527-2 | 2.0 % |
| Flame retardant performance | Test Condition | Test Method | SABIC INNOVATIVE US/UF-1007 BK |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 3.00mm | |
| UL -94 | HB 0.75mm |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/UF-1007 BK |
|---|---|---|---|
| Shrinkage rate | MD | ISO 294-4 | 0.15 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/UF-1007 BK |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 269 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.2E-05 cm/cm/°C |
| TD | ISO 11359-2 | 5.9E-05 cm/cm/°C |