Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
HDPE HD5211EA Dushanzi Petrochemical
--
--
Type, injection molding type
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | Dushanzi Petrochemical/HD5211EA |
|---|---|---|---|
| melt mass-flow rate | 合格 | 9.2-12.8 g/10min | |
| density | 优级 | 949-954 kg/m | |
| melt mass-flow rate | 优级 | 10-12 g/10min | |
| density | 合格 | 949-954 kg/m | |
| melt mass-flow rate | 一等 | 9.7-12.3 g/10min |
| Mechanical properties | Test Condition | Test Method | Dushanzi Petrochemical/HD5211EA |
|---|---|---|---|
| tensile strength | 优级(纵向)，屈服 | >=27 Mpa | |
| Impact strength of cantilever beam gap | 一等（注射） | 7 Kj/m | |
| Environmental stress cracking resistance | 一等 | 25 (50°C)小时 | |
| Impact strength of cantilever beam gap | 合格（压缩） | 4.25 Kj/m | |
| elongation at break | 一等(横向) | >=1200 % | |
| spiral flow length | 420 mm | ||
| Environmental stress cracking resistance | 优级 | 20 (50°C)小时 | |
| tensile strength | 一等(纵向)，屈服 | >=22 Mpa | |
| elongation at break | 优级(横向) | >=1000 % | |
| Impact strength of cantilever beam gap | 优级（压缩） | 5 Kj/m | |
| elongation at break | 合格(纵向) | >=800 % | |
| Flexural modulus | 合格 | >=900 Mpa | |
| tensile strength | 合格(纵向)，屈服 | >=24.3 Mpa | |
| Environmental stress cracking resistance | 合格 | - (50°C)小时 | |
| Flexural modulus | 优级 | >=1150 Mpa | |
| elongation at break | 优级(纵向) | >=1000 % | |
| Flexural modulus | 一等 | >=950 Mpa | |
| elongation at break | 一等(纵向) | >=1100 % | |
| tensile strength | 一等(横向)，屈服 | >=23 Mpa |
| Thermal performance | Test Condition | Test Method | Dushanzi Petrochemical/HD5211EA |
|---|---|---|---|
| vicat | 123 °C |