Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS A310M TORAY JAPAN
Torelina®
Fiber grade
Flame retardant、Glass fiber reinforced、Mineral reinforcement、High rigidity、high strength、High temperature resistan
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/A310M |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 16 kJ/m² |
| Supplementary Information | Test Condition | Test Method | TORAY JAPAN/A310M |
|---|---|---|---|
| BarFlowLength | 320°C,1.00mm | 内部方法 | 9.00 CM |
| hardness | Test Condition | Test Method | TORAY JAPAN/A310M |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 123 |
| Basic performance | Test Condition | Test Method | TORAY JAPAN/A310M |
|---|---|---|---|
| Water absorption rate | ASTM D-570 | 0.02 % |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/A310M |
|---|---|---|---|
| dielectric constant | 23°C,1MHz | IEC 60250 | 5.00 |
| dielectric strength | ASTM D-149 | 15 MV/m | |
| IEC 60243-1 | 22 KV/mm | ||
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| dielectric constant | ASTM D150/IEC 60250 | 5 | |
| Induced positive connection | 10 | ASTM D-150 | 0.002 |
| Inherent resistance of volume | ASTM D-257 | 10 Ω.m | |
| arc resistance | W电极 | ASTM D-495 | 182 秒 |
| Volume resistivity | ASTM D257/IEC 60093 | 1014 Ω.cm | |
| dielectric constant | 10 | ASTM D-150 | 5.8 |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 2E-03 |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/A310M |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 200 kg/cm²(MPa)[Lb/in²] | |
| shear strength | 23°C | JISK7214 | 60.0 Mpa |
| Flexural modulus | ASTM D790/ISO 178 | 22 kg/cm²(MPa)[Lb/in²] | |
| Shore hardness | ASTM D-785 | 123 洛氏 | |
| coefficient of friction | 对钢 | ASTM D-1894 | 0.30 |
| Impact strength of cantilever beam gap | 无缺口23℃ | ASTM D-256 | 20 KJ/m |
| bending strength | ASTM D-790 | 200 Mpa | |
| abrasion | ASTM D-1044 | 70 mg/1000回 | |
| coefficient of friction | 0.30 | ||
| tensile strength | ASTM D-638 | 140 Mpa | |
| Taber abraser | 1000Cycles | ISO 9352 | 70.0 mg |
| elongation at break | ASTM D638/ISO 527 | 0.8 % | |
| limiting pv value | 东丽法 | 815 KJ/m | |
| Rockwell hardness | ASTM D785 | 123 | |
| tensile strength | ASTM D638/ISO 527 | 115 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D-790 | 17.6 GPa | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 0.80 % |
| Impact strength of cantilever beam gap | 缺口23℃ | ASTM D-256 | 90 J/m |
| bending strength | 23°C | ISO 178 | 200 Mpa |
| elongation at break | ASTM D-732 | 60 | |
| tensile strength | ASTM D-638 | 1.2 % | |
| 屈服,23°C | ISO 527-2 | 115 Mpa | |
| Flexural modulus | 23°C | ISO 178 | 22000 Mpa |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 16 kg·cm/cm(J/M)ft·lb/in |
| other | Test Condition | Test Method | TORAY JAPAN/A310M |
|---|---|---|---|
| characteristic | 高硬度 | ||
| Color | 本色.黑 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/A310M |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.5 % | |
| density | ASTM D792/ISO 1183 | 2.06 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.02 % |
| flammability | Test Condition | Test Method | TORAY JAPAN/A310M |
|---|---|---|---|
| UL flame retardant rating | 0.36mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TORAY JAPAN/A310M |
|---|---|---|---|
| Shrinkage rate | 流动方向 | 东丽法 | 0.15 % |
| TD:3.00mm2 | 内部方法 | 0.50 % | |
| MD:3.00mm4 | 内部方法 | 0.20 % | |
| 320℃,98MPa,1mm厚，流动长 | 东丽法 | 90 | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.020 % |
| Shrinkage rate | 垂重方向 | 东丽法 | 0.55 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/A310M |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 278 °C | |
| Combustibility (rate) | UL 94 | V-0 | |
| Linear coefficient of thermal expansion | 垂重方向 | ASTM D-696 | 2.4 |
| Heat distortion temperature | 1.82MPa，HDT | ASTM D-648 | >260 °C |
| combustibility | UL -94 | V-0 | |
| Linear coefficient of thermal expansion | 流动方向 | ASTM D-696 | 1.6 |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 260 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.9E-05 cm/cm/°C |
| melting temperature | DSC | 278 °C | |
| 278 ℃（℉） | |||
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 2E-05 cm/cm/°C |
| ASTM D696/ISO 11359 | 1.9 mm/mm.℃ |