Certificates
PC G-3430RH BK TEIJIN JAPAN
PANLITE®
machine、Mechanical components
Glass fiber reinforced、High rigidity、Good demolding performanc、Type: Standard
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | TEIJIN JAPAN/G-3430RH BK |
|---|---|---|---|
| Water absorption rate | 24hr，in 23℃ | ASTM D-570 | 0.12 % |
| Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/G-3430RH BK |
|---|---|---|---|
| Tensile modulus | ASTM D-638 | 8240(84000) MPa(Kgf/cm | |
| elongation | 断裂 | ASTM D-638 | 3.5 % |
| bending strength | ASTM D-790 | 186(1900) MPa(Kgf/cm | |
| Rockwell hardness | ASTM D-785 | 93 M标度 | |
| Impact strength of cantilever beam gap | 艾氏、带缺口厚度6.4mm | ASTM D-256 | 157(16) J/m(kgf·cm/cm) |
| 艾氏、带缺口厚度3.2mm | ASTM D-256 | 157(16) J/m(kgf·cm/cm) | |
| compressive strength | ASTM D-695 | 157(1600) MPa(Kgf/cm | |
| tensile strength | ASTM D-638 | 126(1280) MPa(Kgf/cm | |
| Flexural modulus | ASTM D-790 | 7260(74000) MPa(Kgf/cm | |
| dielectric strength | 快速加压值厚度1.6mm | ASTM D-149 | 30 KV/mm |
| Electrical performance | Test Condition | Test Method | TEIJIN JAPAN/G-3430RH BK |
|---|---|---|---|
| dielectric constant | 60Hz | ASTM D-150 | 3.51 |
| Dielectric loss | 10，正切 | ASTM D-150 | 0.009 |
| Volume resistivity | ASTM D-257 | 1×10 Ω.cm | |
| Conductive Track Resistance (CTI) | IEC 112 | 180 V | |
| arc resistance | ASTM D-495 | 100 sec | |
| Dielectric loss | 60Hz，正切 | ASTM D-150 | 0.0008 |
| dielectric constant | 10 | ASTM D-150 | 3.41 |
| physical property | Test Condition | Test Method | TEIJIN JAPAN/G-3430RH BK |
|---|---|---|---|
| Shrinkage rate | 流动方向 | ASTM D-955 | 0.02-0.2 % |
| 垂直方向 | ASTM D-955 | 0.3-0.5 % |
| Thermal performance | Test Condition | Test Method | TEIJIN JAPAN/G-3430RH BK |
|---|---|---|---|
| Heat distortion temperature | 负荷1.813MPa(18.6kgf/cm，HDT | JIS K-7207 | 149 °C |
| 负荷0.451MPa(4.6kgf/cm，HDT | JIS K-7207 | 151 °C | |
| TEMPERATURE | 电学式，厚度1.47mm | UL 746B | 130 °C |
| Linear coefficient of thermal expansion | 垂直方向 | ASTM D-696 | 5.6 |
| 流动方向 | ASTM D-696 | 2.0 | |
| TEMPERATURE | 非冲击式，厚度1.47mm | UL 746B | 130 °C |
| 冲击式，厚度1.47mm | UL 746B | 125 °C |