Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL1810T-7R1D047 SABIC INNOVATIVE US
LEXAN™ 
Plastic bag、3D printing application、Electronic and Electrical
High mobility、Ductility at low temperat、Short molding cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Thermal PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL1810T-7R1D047
RTIUL 746130 °C
Vicat Softening Temperature--ISO 306/B50137 °C
Ball PressureTest123 到 127°CIEC 60695-10-2通过
Linear thermal expansion coefficient流动 : 23 到 80°CISO 11359-26.5E-5 cm/cm/°C
Deflection Temperature Under Load?1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9ISO 75-2/Af117 °C
Vicat Softening Temperature--ASTM D152510138 °C
--ISO 306/B120140 °C
Linear thermal expansion coefficient横向 : -40 到 95°CASTM E8317.4E-5 cm/cm/°C
RTI ElecUL 746130 °C
Deflection Temperature Under Load?1.8 MPa, 未退火, 3.20 mmASTM D648120 °C
Linear thermal expansion coefficient流动 : -40 到 95°CASTM E8316.5E-5 cm/cm/°C
横向 : 23 到 80°CISO 11359-27.4E-5 cm/cm/°C
HardnessTest ConditionTest MethodSABIC INNOVATIVE US/EXL1810T-7R1D047
Rockwell HardnessL 计秤ISO 2039-290
InjectionTest ConditionTest MethodSABIC INNOVATIVE US/EXL1810T-7R1D047
Middle Temperature280 到 305 °C
Drying Time3.0 到 4.0 hr
Suggested Shot Size40 到 60 %
Drying Temperature120 °C
Mold Temperature70 到 95 °C
Vent Depth0.025 到 0.076 mm
Suggested Max Moisture0.020 %
Processing (Melt) Temp295 到 315 °C
Rear Temperature270 到 295 °C
Nozzle Temperature290 到 310 °C
Front Temperature295 到 315 °C
Back Pressure0.300 到 0.700 Mpa
Screw Speed40 到 70 rpm
PhysicalTest ConditionTest MethodSABIC INNOVATIVE US/EXL1810T-7R1D047
Moisture Absorption平衡, 23°C, 50% RHISO 620.090 %
Melt Mass-Flow Rate300°C/1.2 kgASTM D123835 g/10 min
Modeling Shrinkage横向流动 : 3.20 mm内部方法0.40 到 0.80 %
流动 : 3.20 mm内部方法0.40 到 0.80 %
Moisture Absorption饱和, 23°CISO 620.12 %
Melt Volume flow Rate300°C/1.2 kgISO 113333.0 cm3/10min
Mechanical PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL1810T-7R1D047
Tensile Strength断裂ISO 527-2/5056.0 Mpa
Tensile Modulus--ISO 527-2/12400 Mpa
Tensile Elongation断裂 3ASTM D638120 %
Tensile Strength屈服 3ASTM D63859.0 Mpa
Tensile Elongation屈服ISO 527-2/505.4 %
Flexural Modulus50.0 mm 跨距 4ASTM D7902350 Mpa
Tensile Modulus-- 2ASTM D6382360 Mpa
Tensile Strength屈服ISO 527-2/5059.0 Mpa
Flexural Stress屈服, 50.0 mm 跨距 4ASTM D79099.0 Mpa
Tensile Elongation屈服 3ASTM D6385.8 %
Flexural Stress-- 5, 6ISO 17892.0 Mpa
Flexural Modulus-- 5ISO 1782250 Mpa
Tensile Elongation断裂ISO 527-2/50120 %
Tensile Strength断裂 3ASTM D63858.0 Mpa
OpticalTest ConditionTest MethodSABIC INNOVATIVE US/EXL1810T-7R1D047
Haze2540 µmASTM D10033.0 %
Transmittance2540 µmASTM D100382.0 %
Impact PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL1810T-7R1D047
Unnotched Izod Impact Strength23°CISO 180/1U无断裂
Instrumented Dart Impact23°C, Total EnergyASTM D376379.0 J
Charpy Notched Impact Strength-30°CISO 179/1eA40 kJ/m²
23°CISO 179/1eA65 kJ/m²
Charpy Unnotched Impact Strength23°CISO 179/1eU无断裂
Unnotched Izod Impact Strength-30°CISO 180/1U无断裂
Charpy Unnotched Impact Strength-30°CISO 179/1eU无断裂
FlammabilityTest ConditionTest MethodSABIC INNOVATIVE US/EXL1810T-7R1D047
Glow Wire Flammability Index3.0 mmIEC 60695-2-12960 °C
Glow Wire Ignition Temperature0.8 mmIEC 60695-2-13825 °C
3.0 mmIEC 60695-2-13850 °C
UL flame retardant rating1.5 mmUL 94HB
Electrical PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL1810T-7R1D047
Volume ResistivityASTM D257> 1.0E+15 ohms·cm
Surface ResistivityASTM D257> 1.0E+15 ohms