Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS OF006IXQ-7G1B0311 SABIC INNOVATIVE NANSHA
--
--
Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/OF006IXQ-7G1B0311 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 51 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 4.89 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 16 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 13.4 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/OF006IXQ-7G1B0311 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 9820 Mpa | |
| ASTM D638 | 10800 Mpa | ||
| elongation | 断裂 | ASTM D638 | 2.4 % |
| bending strength | ISO 178 | 212 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.0 % |
| Flexural modulus | ISO 178 | 10100 Mpa | |
| bending strength | ASTM D790 | 208 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 143 Mpa |
| 断裂 | ISO 527-2 | 139 Mpa | |
| Flexural modulus | ASTM D790 | 9790 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/OF006IXQ-7G1B0311 |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.23 % |
| MD：24小时 | ASTM D955 | 0.20 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.040 % |
| Shrinkage rate | TD:24小时 | ISO 294-4 | 0.67 % |
| TD：24hr | ASTM D955 | 0.70 % |