Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 SCANAMID 66 A33^E F15 POLYKEMI SWEDEN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | POLYKEMI SWEDEN/SCANAMID 66 A33^E F15 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | kJ/m² | 12 16 |
| -20°C | kJ/m² | 9.0 -- |
| hardness | Test Condition | Test Method | POLYKEMI SWEDEN/SCANAMID 66 A33^E F15 |
|---|---|---|---|
| Shore hardness | 邵氏D,15秒 | 74 -- |
| Mechanical properties | Test Condition | Test Method | POLYKEMI SWEDEN/SCANAMID 66 A33^E F15 |
|---|---|---|---|
| tensile strength | MPa | 115 70.0 | |
| bending strength | MPa | 165 115 | |
| Flexural modulus | 23°C | MPa | 4600 3300 |
| Tensile strain | 断裂 | % | 4.0 7.0 |
| flammability | Test Condition | Test Method | POLYKEMI SWEDEN/SCANAMID 66 A33^E F15 |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | HB -- | |
| Hot filament ignition temperature | 2.0mm | °C | 650 -- |
| physical property | Test Condition | Test Method | POLYKEMI SWEDEN/SCANAMID 66 A33^E F15 |
|---|---|---|---|
| Shrinkage rate | MD | % | 0.40 -- |
| density | g/cm³ | 1.20 -- | |
| Shrinkage rate | TD | % | 1.2 -- |
| Thermal performance | Test Condition | Test Method | POLYKEMI SWEDEN/SCANAMID 66 A33^E F15 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 250 -- |
| 1.8MPa,未退火，HDT | °C | 235 -- | |
| vicat | °C | >200 -- |