ABS+PMMA RONFALIN® RHG12 A SCHULMAN USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | A SCHULMAN USA/RONFALIN® RHG12 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180/1A | 8.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | A SCHULMAN USA/RONFALIN® RHG12 |
|---|---|---|---|
| Flexural modulus | ISO 178 | 2700 MPa | |
| tensile strength | 屈服 | ISO 527-2/50 | 50.0 MPa |
| flammability | Test Condition | Test Method | A SCHULMAN USA/RONFALIN® RHG12 |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | A SCHULMAN USA/RONFALIN® RHG12 |
|---|---|---|---|
| Shrinkage rate | 0.40to0.60 % | ||
| density | ISO 1183 | 1.10 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 12 g/10min |
| Thermal performance | Test Condition | Test Method | A SCHULMAN USA/RONFALIN® RHG12 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 95.0 °C |
| vicat | ISO 306/B50 | 97.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 95.0 °C |