Melt Volume-Flow Rate (MVR)

300°C/1.2kg

ISO1133

cm3/10min

1

Melt mass flow rate

300°C/1.2kg

ASTMD1238

g/10min

1

Shrinkage rate

MD：3.20mm

内部方法

%

0

Water absorption rate

饱和,23°C

ISO62

%

0

Water absorption rate

平衡,23°C,50%RH

ISO62

%

0

Impact strength of simply supported beam gap

-30°C

ISO179/1eA

kJ/m²

1

Impact strength of simply supported beam gap

23°C

ISO179/1eA

kJ/m²

2

Tensile modulus

ASTMD638

Mpa

3

Tensile modulus

ISO527-2/1

Mpa

3

tensile strength

屈服

ASTMD638

Mpa

5

tensile strength

屈服

ISO527-2/5

Mpa

5

tensile strength

断裂

ASTMD638

Mpa

4

tensile strength

断裂

ISO527-2/5

Mpa

4

elongation

屈服

ASTMD638

%

4

elongation

屈服

ISO527-2/5

%

4

elongation

断裂

ASTMD638

%

2

elongation

断裂

ISO527-2/5

%

1

Bending modulus

50.0mm跨距

ASTMD790

Mpa

3

Bending modulus

ISO178

Mpa

3

bending strength

屈服,50.0mm跨距

ASTMD790

Mpa

9

Bending strength 5,

ISO178

Mpa

9

Suspended wall beam gap impact strength

-30°C

ISO180/1A

kJ/m²

1

Suspended wall beam gap impact strength

23°C

ISO180/1A

kJ/m²

2

Dart impact equipped with measuring instruments

23°C,TotalEnergy

ASTMD3763

J

4

Hot deformation temperature

1.8MPa,未退火,3.20mm

ASTMD648

°C

1

Hot deformation temperature

1.8MPa,Unannealed,64.0mmSpan

ISO75-2/Af

°C

1

vicat softening point

ASTMD152510

°C

1

vicat softening point

--

ISO306/B50

°C

1

vicat softening point

--

ISO306/B120

°C

1

Linear coefficient of thermal expansion

MD：-40到40°C

ASTME831

cm/cm/°C

4

Linear coefficient of thermal expansion

MD：-40到40°C

ISO11359-2

cm/cm/°C

4

Linear coefficient of thermal expansion

TD：-40到40°C

ASTME831

cm/cm/°C

6

Linear coefficient of thermal expansion

TD：-40到40°C

ISO11359-2

cm/cm/°C

6

Surface resistivity

ASTMD257

ohms

2

Dielectric strength

1.60mm,inOil

ASTMD149

KV/mm

3

Volume resistivity

ASTMD257

ohms·cm

1