PC
PC SABIC INNOVATIVE NANSHA SLX2271T NA9E166T
High liquidity level
US$ 6,946 / MT
FOB Guangzhou port, China
optical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/SLX2271T NA9E166T
Refractive indexISO 4891.590
transmissivity2540μmASTM D100389.0 %
turbidity2540μmASTM D10030.60 %
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/SLX2271T NA9E166T
bending strengthISO 17896.0 Mpa
elongationBreakASTM D638>100 %
Bending modulus50.0mmSpanASTM D7902450 Mpa
Tensile modulusISO 527-2/12300 Mpa
ASTM D6382400 Mpa
tensile strengthBreakISO 527-2/5070.0 Mpa
YieldISO 527-2/5067.0 Mpa
Tensile strainBreakISO 527-2/50>100 %
bending strengthYield,50.0mmSpanASTM D79096.0 Mpa
tensile strengthBreakASTM D63867.0 Mpa
YieldASTM D63865.0 Mpa
Bending modulusISO 1782450 Mpa
Tensile strainYieldISO 527-2/506.0 %
elongationYieldASTM D6386.0 %
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/SLX2271T NA9E166T
Vicat softening temperature--ISO 306/B50139 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af124 °C
1.8MPa,Unannealed,3.20mmASTM D648124 °C
Linear coefficient of thermal expansionMD：-40to40°CISO 11359-27E-05 cm/cm/°C
MD：-40to40°CASTME8317E-05 cm/cm/°C
TD：-40to40°CASTME8317E-05 cm/cm/°C
Ball Pressure Test125°CIEC 60695-10-2Pass
Vicat softening temperatureASTM D152510139 °C
--ISO 306/B120140 °C
Linear coefficient of thermal expansionTD：-40to40°CISO 11359-27E-05 cm/cm/°C
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/SLX2271T NA9E166T
Burning wire flammability index1.6mmIEC 60695-2-12960 °C
Hot filament ignition temperature3.0mmIEC 60695-2-13825 °C
2.5mmIEC 60695-2-13825 °C
2.0mmIEC 60695-2-13825 °C
UL flame retardant rating1.0mmUL 94V-2
Hot filament ignition temperature1.0mmIEC 60695-2-13825 °C
impact performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/SLX2271T NA9E166T
Charpy Notched Impact Strength-30°CISO 179/1eA15 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A65 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Charpy Notched Impact Strength23°CISO 179/1eA65 kJ/m²
Dart impact23°C,TotalEnergyASTM D376380.0 J
Impact strength of cantilever beam gap-30°CISO 180/1A10 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1UNoBreak
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/SLX2271T NA9E166T
melt mass-flow rate300°C/1.2kgASTM D123818 g/10min
Outdoor applicabilityUL 746Cf2
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
Shrinkage rateMD：3.20mmInternal Method0.50-0.70 %
Water absorption rateSaturation,23°CISO 620.35 %
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 113316.0 cm3/10min