Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LDPE 2426K RABIGH SAUDI
Petro Rabigh
Packaging film
High transparency
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | RABIGH SAUDI/2426K |
|---|---|---|---|
| Dart impact | 50µm,吹塑薄膜 | ASTM D1709 | 120 g |
| elongation | MD:断裂,50µm,吹塑薄膜 | ISO 527-3 | 500 % |
| tensile strength | MD:断裂,50µm,吹塑薄膜 | ISO 527-3 | 20.0 Mpa |
| film thickness | 50 µm | ||
| elongation | TD:断裂,50µm,吹塑薄膜 | ISO 527-3 | 630 % |
| tensile strength | TD:断裂,50µm,吹塑薄膜 | ISO 527-3 | 18.0 Mpa |
| Mechanical properties | Test Condition | Test Method | RABIGH SAUDI/2426K |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 260 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 11.0 Mpa |
| optical performance | Test Condition | Test Method | RABIGH SAUDI/2426K |
|---|---|---|---|
| gloss | 20°,50.0µm,吹塑薄膜 | ASTM D2457 | 80 |
| Haze ratio | 50.0µm,吹塑薄膜 | ASTM D1003 | 8.0 % |
| physical property | Test Condition | Test Method | RABIGH SAUDI/2426K |
|---|---|---|---|
| density | ISO 1183 | 0.924 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 4.0 g/10min |
| Thermal performance | Test Condition | Test Method | RABIGH SAUDI/2426K |
|---|---|---|---|
| vicat | ASTM D1525 | 93.0 °C | |
| melting temperature | ISO 11357-3 | 110 °C |