Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS SF-0505 Samsung Cheil South Korea
STAREX®
Automotive components
Flame retardant、Thermal stability、Aging resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Samsung Cheil South Korea/SF-0505 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.3 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.5 kJ/m² |
| 23°C,3.18mm | ASTM D256 | 110 J/m |
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/SF-0505 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 113 |
| R级 | ASTM D785 | 113 | |
| Hardness | JISK5401 | F |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/SF-0505 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 56.0 Mpa |
| Tensile modulus | ASTM D638 | 2400 Mpa | |
| elongation | 断裂 | ASTM D638 | 11 % |
| Tensile modulus | ISO 527-2/50 | 2400 Mpa | |
| bending strength | ISO 178 | 81.0 Mpa | |
| Flexural modulus | ISO 178 | 2400 Mpa | |
| bending strength | ASTM D790 | 71.0 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 39.0 Mpa |
| 屈服 | ASTM D638 | 50.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 5.6 % |
| Flexural modulus | ASTM D790 | 2300 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 48.0 Mpa |
| flammability | Test Condition | Test Method | Samsung Cheil South Korea/SF-0505 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/SF-0505 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.30-0.60 % |
| density | ASTM D792 | 1.11 g/cm³ | |
| ISO 1183 | 1.11 g/cm³ | ||
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 17 g/10min |
| Shrinkage rate | MD：3.20mm | ISO 2577 | 0.30-0.60 % |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 17 g/10min |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/SF-0505 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 73.0 °C |
| vicat | -- | ISO 306/B120 | 96.0 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 84.0 °C |
| 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 84.0 °C | |
| vicat | -- | ISO 306/B50 | 94.0 °C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 92.0 °C |