ASA KR2863C BASF GERMANY
Luran®S
Fitness equipment、Automotive sector
High temperature resistan、UV resistance、high strength
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/KR2863C |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 60 kJ/m² |
| -30°C | ISO 179 | 17 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 60 kJ/m² |
| -30°C | ISO 180/A | 10 kJ/m² |
| hardness | Test Condition | Test Method | BASF GERMANY/KR2863C |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 110 Mpa |
| film | Test Condition | Test Method | BASF GERMANY/KR2863C |
|---|---|---|---|
| elongation | 断裂 | ISO 527-3 | >50 % |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/KR2863C |
|---|---|---|---|
| dielectric constant | 100Hz | IEC 60250 | 3.10 |
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 6E-03 |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.010 |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/KR2863C |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2500 Mpa | |
| bending strength | ISO 178 | 93.0 Mpa | |
| tensile strength | 屈服,23°C | ISO 527-2 | 62.0 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 4.9 % |
| physical property | Test Condition | Test Method | BASF GERMANY/KR2863C |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.50-0.90 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.16 % |
| 饱和,23°C | ISO 62 | 0.60 % | |
| density | ISO 1183 | 1.16 g/cm³ | |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 7.00 cm3/10min |
| 260°C/5.0kg | ISO 1133 | 18.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/KR2863C |
|---|---|---|---|
| thermal conductivity | DIN 52612 | 0.17 W/m/K | |
| vicat | -- | ISO 306/A50 | 140 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 109 °C |
| vicat | -- | ISO 306/B50 | 130 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7.0E-5到9.0E-5 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 130 °C |