Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA46 TW272B6 DSM JAPAN
Stanyl®
Wear resistant accessorie
wear resistant、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DSM JAPAN/TW272B6 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 50 kJ/m² |
| -30°C | ISO 179/1eU | 50 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DSM JAPAN/TW272B6 |
|---|---|---|---|
| tensile strength | 断裂, 160°C | ISO 527-2 | 110 Mpa |
| Tensile modulus | -- | ISO 527-2 | 24000 Mpa |
| tensile strength | 断裂, 180°C | ISO 527-2 | 100 Mpa |
| Tensile strain | 断裂, 120°C | ISO 527-2 | 3.1 % |
| tensile strength | 断裂 | ISO 527-2 | 240 Mpa |
| Tensile modulus | 180°C | ISO 527-2 | 10500 Mpa |
| tensile strength | 断裂, 120°C | ISO 527-2 | 130 Mpa |
| Tensile modulus | 160°C | ISO 527-2 | 11000 Mpa |
| 120°C | ISO 527-2 | 12500 Mpa | |
| Tensile strain | 断裂, 200°C | ISO 527-2 | 3.1 % |
| 断裂, 180°C | ISO 527-2 | 3.1 % | |
| 断裂 | ISO 527-2 | 1.6 % | |
| 断裂, 160°C | ISO 527-2 | 3.1 % | |
| Tensile modulus | 200°C | ISO 527-2 | 10000 Mpa |
| tensile strength | 断裂, 200°C | ISO 527-2 | 90.0 Mpa |
| physical property | Test Condition | Test Method | DSM JAPAN/TW272B6 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 2.3 % |
| Shrinkage rate | 流量 | ISO 294-4 | 0.30 % |
| 横向流量 | ISO 294-4 | 0.60 % |
| Thermal performance | Test Condition | Test Method | DSM JAPAN/TW272B6 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 295 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 290 °C |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 2.5E-5 cm/cm/°C |
| 横向 | ISO 11359-2 | 3.5E-5 cm/cm/°C |