TPEE PELPRENE™ S1002 TOYOBO CO., LTD.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodTOYOBO CO., LTD./PELPRENE™ S1002
Impact strength of cantilever beam gapASTM D256无断裂
Supplementary InformationTest ConditionTest MethodTOYOBO CO., LTD./PELPRENE™ S1002
ResilienceJISK630163 %
hardnessTest ConditionTest MethodTOYOBO CO., LTD./PELPRENE™ S1002
Shore hardness邵氏DASTM D224048
邵氏AJISK630196
Electrical performanceTest ConditionTest MethodTOYOBO CO., LTD./PELPRENE™ S1002
Volume resistivityASTM D2572E+12 ohms·cm
dielectric strengthJISK211125 kV/mm
Mechanical propertiesTest ConditionTest MethodTOYOBO CO., LTD./PELPRENE™ S1002
Taber abraser1000CyclesASTM D104415.0 mg
tensile strength --ASTM D63830.0 MPa
elongation断裂ASTM D638720 %
compressive strength10%应变ASTM D69510.2 MPa
tensile strength 50%应变ASTM D63810.8 MPa
Flexural modulusASTM D790108 MPa
flammabilityTest ConditionTest MethodTOYOBO CO., LTD./PELPRENE™ S1002
UL flame retardant ratingUL 94HB
physical property Test ConditionTest MethodTOYOBO CO., LTD./PELPRENE™ S1002
Shrinkage rateMD：2.00mmASTM D9551.2 %
Water absorption rate平衡,23°C,65%RHASTM D5700.40 %
melt mass-flow rate230°C/2.16kgASTM D123817 g/10min
densityASTM D7921.21 g/cm³
elastomerTest ConditionTest MethodTOYOBO CO., LTD./PELPRENE™ S1002
compression setJISK630160 %
tear strengthASTM D624118 kN/m
Thermal performanceTest ConditionTest MethodTOYOBO CO., LTD./PELPRENE™ S1002
Heat distortion temperature1.8MPa,未退火，HDTASTM D64868.0 °C
vicatASTM D1525172 °C
brittle temperatureJISK6301<-65.0 °C
melting temperatureDSC200 °C
Linear coefficient of thermal expansionMDASTME8311.9E-04 cm/cm/°C