Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL9330-BL1B483 SABIC INNOVATIVE US
LEXAN™
Casters、Thin walled products、food
Flame retardant、Toughening、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9330-BL1B483 |
|---|---|---|---|
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 11 | ISO 75-2/Ae | 124 °C |
| RTI | UL 746 | 125 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 124 °C |
| Linear thermal expansion coefficient | 横向 : -40 到 40°C | ASTM E831 | 6.7E-5 cm/cm/°C |
| Vicat Softening Temperature | -- | ISO 306/B50 | 140 °C |
| RTI Elec | UL 746 | 125 °C | |
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831 | 6.7E-5 cm/cm/°C |
| 横向 : 23 到 80°C | ISO 11359-2 | 7.7E-5 cm/cm/°C | |
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 11 | ISO 75-2/Be | 135 °C |
| Ball PressureTest | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Linear thermal expansion coefficient | 流动 : 23 到 80°C | ISO 11359-2 | 7.2E-5 cm/cm/°C |
| RTI Imp | UL 746 | 115 °C | |
| Vicat Softening Temperature | -- | ASTM D152512, ISO 306/B12012 | 142 °C |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 120 °C |
| 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 134 °C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9330-BL1B483 |
|---|---|---|---|
| Ball Indentation Hardness | H 358/30 | ISO 2039-1 | 90.0 Mpa |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9330-BL1B483 |
|---|---|---|---|
| Middle Temperature | 280 到 305 °C | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Suggested Shot Size | 40 到 60 % | ||
| Drying Temperature | 120 °C | ||
| Mold Temperature | 70 到 95 °C | ||
| Vent Depth | 0.025 到 0.076 mm | ||
| Suggested Max Moisture | 0.020 % | ||
| Processing (Melt) Temp | 295 到 315 °C | ||
| Rear Temperature | 215 到 295 °C | ||
| Nozzle Temperature | 290 到 310 °C | ||
| Front Temperature | 295 到 315 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 40 到 70 rpm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9330-BL1B483 |
|---|---|---|---|
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.15 % |
| Density / Specific Gravity | -- | ASTM D792 | 1.18 g/cm³ |
| -- | ISO 1183 | 1.19 g/cm³ | |
| Melt Mass-Flow Rate | 300°C/1.2 kg | ASTM D1238 | 10 g/10 min |
| Outdoor Suitability | UL 746C | f1 | |
| Modeling Shrinkage | 横向流动 : 3.20 mm | 内部方法 | 0.40 到 0.80 % |
| 流动 : 3.20 mm | 内部方法 | 0.40 到 0.80 % | |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.35 % |
| Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 9.00 cm3/10min |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9330-BL1B483 |
|---|---|---|---|
| Tensile Strength | 断裂 | ISO 527-2/50 | 60.0 Mpa |
| Tensile Modulus | -- | ISO 527-2/1 | 2100 Mpa |
| Tensile Elongation | 断裂 3 | ASTM D638 | 130 % |
| Tensile Strength | 屈服 3 | ASTM D638 | 58.0 Mpa |
| Tensile Elongation | 屈服 | ISO 527-2/50 | 6.0 % |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 2060 Mpa |
| Tensile Modulus | -- 2 | ASTM D638 | 2100 Mpa |
| Tensile Strength | 屈服 | ISO 527-2/50 | 55.0 Mpa |
| Flexural Stress | 屈服, 50.0 mm 跨距 4 | ASTM D790 | 88.0 Mpa |
| Tensile Elongation | 屈服 3 | ASTM D638 | 6.0 % |
| Flexural Stress | -- 5, 6 | ISO 178 | 85.0 Mpa |
| Flexural Modulus | -- 5 | ISO 178 | 2200 Mpa |
| Tensile Elongation | 断裂 | ISO 527-2/50 | 130 % |
| Tensile Strength | 断裂 3 | ASTM D638 | 61.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9330-BL1B483 |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ISO 180/1U | 无断裂 |
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 52.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 60 kJ/m² |
| 23°C | ISO 179/1eA | 75 kJ/m² | |
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 无断裂 |
| Unnotched Izod Impact Strength | -30°C | ISO 180/1U | 无断裂 |
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 无断裂 |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9330-BL1B483 |
|---|---|---|---|
| Glow Wire Ignition Temperature | 1.0 mm | IEC 60695-2-13 | 825 °C |
| UL flame retardant rating | 3.0 mm | UL 94 | 5VA |
| Oxygen Index | ISO 4589-2 | 35 % | |
| Glow Wire Flammability Index | 1.0 mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9330-BL1B483 |
|---|---|---|---|
| Dissipation Factor? | 60 Hz | IEC 60250 | 1.0E-3 |
| Dielectric Constant | 50 kHz | ASTM D150 | 2.95 |
| 60 Hz | IEC 60250 | 2.60 | |
| Dielectric Strength | 3.20 mm, in Oil | ASTM D149 | 17 KV/mm |
| Dissipation Factor? | 50 Hz | ASTM D150 | 2.4E-3 |
| High Amp Arc Ignition | UL 746 | PLC 0 | |
| Volume Resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| Hot-wire Ignition | UL 746 | PLC 1 | |
| Dielectric Constant | 1 MHz | ASTM D150 | 2.90 |
| 60 Hz | ASTM D150 | 2.95 | |
| 50 Hz | IEC 60250 | 2.60 | |
| Dissipation Factor? | 1 MHz | ASTM D150, IEC 60250 | 8.5E-3 |
| Dielectric Strength | 3.20 mm, 在油中 | IEC 60243-1 | 16 KV/mm |
| Dissipation Factor? | 50 Hz | IEC 60250 | 1.0E-3 |
| Comparative Tracking Index | UL 746 | PLC 3 | |
| Dissipation Factor? | 60 Hz | ASTM D150 | 2.4E-3 |
| Comparative Tracking Index | IEC 60112 | 225 V | |
| Dielectric Constant | 1 MHz | IEC 60250 | 2.70 |