LCP L304M35 TORAY JAPAN
SIVERAS™
Electrical components、Electrical appliances
Low warpage、High mobility、Good liquidity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/L304M35 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 60 J/m |
| hardness | Test Condition | Test Method | TORAY JAPAN/L304M35 |
|---|---|---|---|
| Rockwell hardness | R 级 | ASTM D785 | 105 |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/L304M35 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 2.5 % |
| bending strength | ASTM D790 | 160 Mpa | |
| Flexural modulus | ASTM D790 | 13000 Mpa | |
| tensile strength | ASTM D638 | 125 Mpa |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/L304M35 |
|---|---|---|---|
| dielectric strength | ASTM D149 | 58 KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| dielectric constant | ASTM D150 | 4.10 |
| flammability | Test Condition | Test Method | TORAY JAPAN/L304M35 |
|---|---|---|---|
| UL flame retardant rating | 0.38 mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TORAY JAPAN/L304M35 |
|---|---|---|---|
| Water absorption rate | 24 hr, 23°C | ASTM D570 | 0.010 % |
| Shrinkage rate | 横向流量 : 1.00 mm | 内部方法 | 0.55 % |
| density | ASTM D792 | 1.68 g/cm³ | |
| Shrinkage rate | 流量 : 1.00 mm | 内部方法 | 0.14 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/L304M35 |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ASTM D648 | 270 °C |
| Linear coefficient of thermal expansion | 流动 | ASTM D696 | 8.0E-6 - 1.9E-5 cm/cm/°C |