PP Copolymer WINTEC™ WMX03 Japan Polychem Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Japan Polychem Corporation/WINTEC™ WMX03 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 8.0 kJ/m² |
| 0°C | ISO 179 | 2.0 kJ/m² |
| hardness | Test Condition | Test Method | Japan Polychem Corporation/WINTEC™ WMX03 |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 70 |
| Mechanical properties | Test Condition | Test Method | Japan Polychem Corporation/WINTEC™ WMX03 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2 | >400 % | |
| Tensile modulus | ISO 527-2 | 750 MPa | |
| tensile strength | 屈服 | ISO 527-2 | 22.0 MPa |
| Flexural modulus | ISO 178 | 750 MPa | |
| bending strength | ISO 178 | 25.0 MPa |
| optical performance | Test Condition | Test Method | Japan Polychem Corporation/WINTEC™ WMX03 |
|---|---|---|---|
| gloss | ASTM D523 | 90 | |
| Haze ratio | 1000µm | ISO 14782 | 10 % |
| 2000µm | ISO 14782 | 25 % |
| physical property | Test Condition | Test Method | Japan Polychem Corporation/WINTEC™ WMX03 |
|---|---|---|---|
| spiral flow length | 内部方法 | 74.0 cm | |
| melt mass-flow rate | ISO 1133 | 25 g/10min | |
| Shrinkage rate | 内部方法 | 1.0to1.4 % | |
| density | ISO 1183 | 0.900 g/cm³ |
| Thermal performance | Test Condition | Test Method | Japan Polychem Corporation/WINTEC™ WMX03 |
|---|---|---|---|
| vicat | ISO 306 | 110 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 70.0 °C |