Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC IR2200 CB FIPC TAIWAN
TARFLON™
Thin walled products
Low viscosity、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | FIPC TAIWAN/IR2200 CB |
|---|---|---|---|
| melt mass-flow rate | 300℃ 1.2kg | ISO 1133 (ASTM D-1238) | 12 g/10min |
| Water absorption rate | 23℃水中24h | ASTM D-570 | 0.23 % |
| density | ASTM D-792 | 1.2 g/cm |
| Mechanical properties | Test Condition | Test Method | FIPC TAIWAN/IR2200 CB |
|---|---|---|---|
| ISO R-527 (ASTM D-638) | 64 Mpa | ||
| IZOD impact strength | 4mm with notch 3.2mm with notch | ISO 180 (ASTM D-256) | 70 KJ/m |
| Tensile elasticity | ISO R-527 (ASTM D-638) | 2300 Mpa | |
| Tensile strength | ISO R-527 (ASTM D-638) | 68 Mpa | |
| Tensile failure rate | ISO R-527 (ASTM D-638) | 115 % | |
| Taber wear amount | 1,000round | ASTM D-1044 | 12 mg |
| Rockwell hardness | ISO 2039-2 (ASTM D-785) | 120 R | |
| ISO 178 (ASTM D-790) | 93 Mpa |
| processability | Test Condition | Test Method | FIPC TAIWAN/IR2200 CB |
|---|---|---|---|
| Forming shrinkage rate | ASTM D-955 | 0.5-0.7 % |
| physical property | Test Condition | Test Method | FIPC TAIWAN/IR2200 CB |
|---|---|---|---|
| Light transmittance | 3mm厚 | ASTM D-1003 | 85-89 % |
| Thermal performance | Test Condition | Test Method | FIPC TAIWAN/IR2200 CB |
|---|---|---|---|
| vicat | ISO 306 | 148 °C | |
| linear expansion coefficient | ASTM D-696 (ASTM D-695) | 6.5 ×10 | |
| 1.8Mpa 18.6kg/cm | ISO 75 (ASTM D-648) | 132 °C | |
| combustibility | 1.47mm厚 | UL-94 | V-2 |