Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO N1150 SABIC INNOVATIVE SHANGHAI
NORYL™
Dash board、Electronic field、Electrical field、Plastic bag
heat-resisting、Low Specific Gravity、Impact resistance、Dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/N1150 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 6.0 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 40.0 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 4.0 kJ/m² |
| 23°C | ISO 180/1A | 6.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/N1150 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2650 Mpa | |
| elongation | 屈服 | ASTM D638 | 4.0 % |
| tensile strength | 断裂 | ASTM D638 | 55.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 3.5 % |
| tensile strength | 断裂 | ISO 527-2/50 | 52.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 3050 Mpa |
| Tensile modulus | ASTM D638 | 2700 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 72.0 Mpa |
| elongation | 断裂 | ASTM D638 | 8.0 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 117 Mpa |
| ISO 178 | 105 Mpa | ||
| Flexural modulus | ISO 178 | 2600 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 75.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 7.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/N1150 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/N1150 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| melt mass-flow rate | 280°C/5.0kg | ASTM D1238 | 15 g/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.070 % |
| Melt volume flow rate | 280°C/5.0kg | ISO 1133 | 15.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/N1150 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 132 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 5.8E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 5.8E-05 cm/cm/°C | |
| vicat | -- | ISO 306/B50 | 130 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 5.5E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 5.5E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 109 °C |
| vicat | ASTM D152510 | 130 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 108 °C |