Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC L-1225L TEIJIN JAPAN
PANLITE®
Electrical appliances、Electrical field、Electronic field
High mobility、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodTEIJIN JAPAN/L-1225L
Impact strength of simply supported beam without notchISO 179NoBreak
Mechanical propertiesTest ConditionTest MethodTEIJIN JAPAN/L-1225L
Tensile modulusISO 527-2/12400 Mpa
bending strengthASTM D790/ISO 17893 kg/cm²(MPa)[Lb/in²]
tensile strength 屈服ISO 527-2/5061.0 Mpa
Flexural modulusASTM D790/ISO 1782350 kg/cm²(MPa)[Lb/in²]
bending strengthISO 17893.0 Mpa
Flexural modulusISO 1782350 Mpa
elongationASTM D638/ISO 5276 %
Tensile modulusASTM D638/ISO 5272400 kg/cm²(MPa)[Lb/in²]
elongation at breakASTM D638/ISO 527>50 %
Tensile strain屈服ISO 527-2/506.0 %
Nominal tensile fracture strainISO 527-2/50>50 %
Electrical performanceTest ConditionTest MethodTEIJIN JAPAN/L-1225L
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 2
Surface ResistivityASTM D257/IEC 60093>1×1015 Ω
dielectric strengthIEC 60243-130 KV/mm
Volume resistivityIEC 60093>1.0E+15 ohms·cm
relative permittivity100HzIEC 602503.10
Dissipation Factor100HzIEC 602501E-03
dielectric constantASTM D150/IEC 602503.1
relative permittivity1MHzIEC 602503.00
arc resistanceASTM D495/IEC 6011230
Surface ResistivityIEC 60093>1.0E+15 ohms
Volume resistivityASTM D257/IEC 60093>1×1013 Ω.cm
Dissipation Factor1MHzIEC 602509E-03
optical performance Test ConditionTest MethodTEIJIN JAPAN/L-1225L
transmissivity3000µmASTM D100388.0 %
refractive indexASTM D542/ISO 4891.585
ASTM D5421.585
transmittanceASTM D1003/ISO 1346888 %
Physical propertiesTest ConditionTest MethodTEIJIN JAPAN/L-1225L
Shrinkage rateASTM D9550.5-0.7 %
Water absorption rateASTM D570/ISO 620.2 %
flammabilityTest ConditionTest MethodTEIJIN JAPAN/L-1225L
UL flame retardant rating1.9mmUL 94HB
Burning wire flammability index3.0mmIEC 60695-2-12960 °C
Hot filament ignition temperature3.0mmIEC 60695-2-13850 °C
Burning wire flammability index1.5mmIEC 60695-2-12850 °C
Hot filament ignition temperature1.5mmIEC 60695-2-13875 °C
UL flame retardant rating0.40mmUL 94V-2
physical property Test ConditionTest MethodTEIJIN JAPAN/L-1225L
Water absorption rate23°C,24hrISO 620.20 %
Melt volume flow rate300°C/1.2kgISO 113318.0 cm3/10min
Shrinkage rateMD:4.00mm内部方法0.50-0.70 %
TD:4.00mm内部方法0.50-0.70 %
Thermal performanceTest ConditionTest MethodTEIJIN JAPAN/L-1225L
RTI Imp1.5mmUL 746115 °C
vicatASTM D1525/ISO R306146 ℃（℉）
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B139 °C
vicatISO 306/B50146 °C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A126 °C
RTI Str1.5mmUL 746125 °C
Linear coefficient of thermal expansionMDISO 11359-27E-05 cm/cm/°C
RTI Elec1.5mmUL 746125 °C
Linear coefficient of thermal expansionTDISO 11359-27E-05 cm/cm/°C
ASTM D696/ISO 113590.7 mm/mm.℃