Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC G-3410R TEIJIN JAPAN
PANLITE®
Engineering accessories
Glass fiber reinforced,High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TEIJIN JAPAN/G-3410R |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 55 kJ/m² |
| Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/G-3410R |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 118(1200) kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO 527-2/1 | 3700 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 70.0 Mpa |
| Flexural modulus | ASTM D790/ISO 178 | 3530(36000) kg/cm²(MPa)[Lb/in²] | |
| bending strength | ISO 178 | 120 Mpa | |
| Flexural modulus | ISO 178 | 3600 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 3.5 % |
| Tensile modulus | ASTM D638/ISO 527 | 3630(37000) kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 78(8) kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 4.0 % | |
| tensile strength | ASTM D638/ISO 527 | 76(770) kg/cm²(MPa)[Lb/in²] |
| Electrical performance | Test Condition | Test Method | TEIJIN JAPAN/G-3410R |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.20 |
| Dissipation Factor | 100Hz | IEC 60250 | 1E-03 |
| relative permittivity | 1MHz | IEC 60250 | 3.20 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 9E-03 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| other | Test Condition | Test Method | TEIJIN JAPAN/G-3410R |
|---|---|---|---|
| characteristic | 易脱模型 |
| Physical properties | Test Condition | Test Method | TEIJIN JAPAN/G-3410R |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.27 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.16 % |
| flammability | Test Condition | Test Method | TEIJIN JAPAN/G-3410R |
|---|---|---|---|
| UL flame retardant rating | 0.43mm | UL 94 | HB |
| 3.0mm | UL 94 | V-1 | |
| 0.8mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | TEIJIN JAPAN/G-3410R |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.16 % |
| Shrinkage rate | MD:4.00mm | 内部方法 | 0.30-0.50 % |
| TD:4.00mm | 内部方法 | 0.40-0.60 % |
| Thermal performance | Test Condition | Test Method | TEIJIN JAPAN/G-3410R |
|---|---|---|---|
| RTI Imp | 1.5mm | UL 746 | 120 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 149 °C |
| vicat | ISO 306/B50 | 151 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 144 °C |
| RTI Str | 1.5mm | UL 746 | 130 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 4E-05 cm/cm/°C |
| RTI Elec | 1.5mm | UL 746 | 130 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 6E-05 cm/cm/°C |