PC/ABS C7230P BK1D605 PC/ABS vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PC/ABS SABIC INNOVATIVE US C7230P BK1D605

Injection grade

US$ 2,708 / MT

FOB China Main Port

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE US/C7230P BK1D605
Hot deformation temperature	1.8 MPa	Flatw 80104 sp=64mm; ISO 75/Af	89
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	59 µm/m-°C
Vicat softening temperature		Equate	110
Linear coefficient of thermal expansion	Flow	ISO 11359-2	42 µm/m-°C
		Across Flow	GB 1040	49 µm/m-°C
		Flow	GB 1040	42 µm/m-°C
UL flame retardant rating		UL 94	V-0
Vicat softening temperature		Rate B/50; ISO 306	107
Vicat softening temperature			Rate B/50; ASTM D1525	108
Hot deformation temperature	1.8 MPa	ASTMF1249	88
mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE US/C7230P BK1D605
elongation at yield		ISO 178	3.8 %
Bending modulus		2 mm/min; ISO 178	4.58
elongation at yield	Type I, 50 mm/min	ASTM D638	4 %
tensile strength	Yield	ISO 178	35 Mpa
Tensile modulus		1 mm/min; ISO 527	5.58
Charpy Notched Impact Strength		Edgew 80104 sp=62mm; ISO 179/1eA	0.5 J/cm²
Elongation at Break	Break	ISO 178	30 %
Bending modulus	1.3 mm/min, 50 mm span	ASTM D790	4.53
bending strength	1.3 mm/min, 50 mm span	ASTM D790	98 Mpa
Impact strength of cantilever beam gap		80104; ISO 180/1A	5 kJ/m²
tensile strength	Type I, 50 mm/min，Yield	ASTM D638	45 Mpa
Impact strength of cantilever beam gap		ASTM D256	0.69 J/cm
bending strength		2 mm/min; ISO 178	99 Mpa
Impact strength of cantilever beam gap			@Temperature -30.0
Elongation at Break	Type I, 50 mm/min，Break	ASTM D638	32 %
Tensile modulus		GB/T 15585-1995	5.2
Physical properties	Test Condition	Test Method	SABIC INNOVATIVE US/C7230P BK1D605
Water absorption rate	Saturation	ISO 62	0.09 %
Compound melt index		MVR [cm^3/10 min]; ISO 1133	49.0 µm/m-°C g/10 min
melt mass-flow rate		ASTM D1238	13
Compound melt index			@Load 2.16 kg. Temperature 260
Shrinkage rate	Flow	SABIC method	0.0025 - 0.0035 cm/cm
Water absorption rate		23°C / 50% RH; ISO 62	0.04 %