Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA CR7020-GY1B299 SABIC INNOVATIVE US
GELOY™
--
High impact resistance、Weather resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/CR7020-GY1B299 |
|---|---|---|---|
| Dart impact | 23°C, Total Energy | ASTM D3763 | 25.0 J |
| N | 107 J/cm |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/CR7020-GY1B299 |
|---|---|---|---|
| Rockwell hardness | R 级 | ASTM D785 | 86 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/CR7020-GY1B299 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 1790 Mpa | |
| elongation | 断裂 | ASTM D638 | 40 % |
| bending strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 58.0 Mpa |
| tensile strength | 断裂 | ASTM D638 | 34.0 Mpa |
| 屈服 | ASTM D638 | 41.0 Mpa | |
| Flexural modulus | 50.0 mm 跨距 | ASTM D790 | 1790 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/CR7020-GY1B299 |
|---|---|---|---|
| dielectric strength | 3.20 mm, in Oil | ASTM D149 | 16 KV/mm |
| Surface Resistivity | ASTM D257 | > 1.0E+15 ohms | |
| dielectric constant | 60 Hz | ASTM D150 | 5.20 |
| Dissipation Factor | 60 Hz | ASTM D150 | 0.15 |
| 50 Hz | ASTM D150 | 0.15 | |
| dielectric constant | 1 MHz | ASTM D150 | 3.21 |
| Hot wire ignition (HWI) | UL 746 | PLC 3 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 0 | |
| Dissipation Factor | 1 MHz | ASTM D150 | 0.026 |
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| dielectric constant | 50 kHz | ASTM D150 | 5.20 |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/CR7020-GY1B299 |
|---|---|---|---|
| gloss | 60°, 无织构 | ASTM D523 | 95 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/CR7020-GY1B299 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/CR7020-GY1B299 |
|---|---|---|---|
| melt mass-flow rate | 220°C/10.0 kg | ASTM D1238 | 7.0 g/10 min |
| Water absorption rate | 平衡, 23°C | ASTM D570 | 0.55 % |
| Outdoor applicability | UL 746C | f2 | |
| melt mass-flow rate | 260°C/5.0 kg | ASTM D1238 | 13 g/10 min |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/CR7020-GY1B299 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 8.6E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 退火，HDT | ASTM D648 | 95.0 °C |
| 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 87.0 °C | |
| Linear coefficient of thermal expansion | 流动 : -30 到 0°C | ASTM E831 | 8.5E-5 cm/cm/°C |
| RTI | UL 746 | 50.0 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 90.0 °C |
| vicat | ASTM D15256 | 99.0 °C | |
| Linear coefficient of thermal expansion | 流动 : 0 到 100°C | ASTM E831 | 9.0E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 79.0 °C |
| RTI Imp | UL 746 | 50.0 °C | |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 9.2E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 76.0 °C |
| RTI Elec | UL 746 | 50.0 °C |