PBT 4602Z NC CELANESE USA
CELANEX®
Electrical applications、Automotive Applications
High toughness、Hydrolysis resistance、Thermal stability、Weather resistance、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | CELANESE USA/4602Z NC |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | ISO 179/1eU | NB KJ/m |
| Impact strength of cantilever beam gap | -30℃ | ISO 180/1A | 10 KJ/m |
| 23℃ | ISO 180/1A | NB KJ/m | |
| Flexural modulus | 23℃ | ISO 178 | 1400 Mpa |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 70 KJ/m |
| -30℃ | ISO 179/1eA | 10 KJ/m | |
| Impact strength of simply supported beam without notch | -30℃ | ISO 179/1eU | NB KJ/m |
| Tensile modulus | 1mm/min | ISO 527-2/1A | 1500 Mpa |
| Tensile stress | 50mm/min，屈服 | ISO 527-2/1A | 40 Mpa |
| Tensile modulus | 50mm/min，屈服 | ISO 527-2/1A | 6 % |
| Rockwell hardness | ISO 2039-2 | 101 M | |
| bending strength | 23℃ | ISO 178 | 45 Mpa |
| Electrical performance | Test Condition | Test Method | CELANESE USA/4602Z NC |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 24 KV/mm | |
| Volume resistivity | 1MHz | IEC 60250 | 3.9 |
| Dielectric dissipation factor | 100Hz | IEC 60250 | 75 E-4 |
| 1MHz | IEC 60250 | 310 E-4 | |
| Volume resistivity | 100Hz | IEC 60250 | 4.4 |
| Surface Resistivity | IEC 60093 | 1E+14 Ohm | |
| Volume resistivity | IEC 60093 | 1E+12 ohm.m | |
| Compared to the Leakage Traceability Index (CTI) | IEC 60112 | 600 |
| physical property | Test Condition | Test Method | CELANESE USA/4602Z NC |
|---|---|---|---|
| Water absorption rate | 23℃,50%相对湿度 | ISO 62 | 0.2 % |
| Shrinkage rate | 横向 | ISO 294-4 | 1.7-2.2 % |
| Melt volume flow rate | ISO 1133 | 9 CM | |
| Water absorption rate | 23℃,饱和 | ISO 62 | 0.45 % |
| Shrinkage rate | 纵向 | ISO 294-4 | 1.7-2.2 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/4602Z NC |
|---|---|---|---|
| Glass Transition Temperature | ISO 11357-1 | 60 °C | |
| Heat distortion temperature | 1.8Mpa，HDT | ISO 75-1/-2 | 48 °C |
| 0.45Mpa，HDT | ISO 75-1/-2 | 110 °C | |
| vicat | ISO 306 | 130 °C | |
| melting temperature | ISO 11357-1 | 225 °C | |
| Linear coefficient of thermal expansion | 纵向 | ISO 11359-2 | 1.3 E-4/℃ |
| UL flame retardant rating | UL 94 | HB |