PBT FG6134 NC010 DUPONT USA
Cristin®
Automotive components,Electronic and electrical components
High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | DUPONT USA/FG6134 NC010 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 60.0 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 50.0 °C | |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 115 °C | |
| 0.45MPa,退火，HDT | ISO 75-2/B | 180 °C | |
| melting temperature | ISO 11357-3 | 225 °C |
| mechanical properties | Test Condition | Test Method | DUPONT USA/FG6134 NC010 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2 | 45 % | |
| Tensile modulus | ISO 527-2 | 2600 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 59.0 Mpa |
| bending strength | ISO 178 | 85.0 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 4.0 % |
| Physical properties | Test Condition | Test Method | DUPONT USA/FG6134 NC010 |
|---|---|---|---|
| shrinkage rate | TD | ISO 294-4 | 1.6 % |
| Ejection Temperature | 170 °C | ||
| melt mass-flow rate | 250°C/2.16kg | ISO 1133 | 34 g/10min |
| shrinkage rate | MD | ISO 294-4 | 1.6 % |
| flammability | Test Condition | Test Method | DUPONT USA/FG6134 NC010 |
|---|---|---|---|
| FMVSS flammability | FMVSS302 | B | |
| Flammability level | 1.5mm | IEC 60695-11-10,-20 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 22 % | |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |