Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
Phenolic LONGLITE® PMC T 385J Chang Chun Plastics Co., Ltd. (CCP Group)
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Chang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PMC T 385J |
|---|---|---|---|
| Charpy Notched Impact Strength | -- | ASTM D256 | 3.4 kN/m |
| Impact strength of cantilever beam gap | -- | JISK6911 | 2.9 kN/m |
| -- | ASTM D256 | 2.9 kN/m | |
| Charpy Notched Impact Strength | -- | JISK7111 | 3.4 kN/m |
| Supplementary Information | Test Condition | Test Method | Chang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PMC T 385J |
|---|---|---|---|
| shelf-life | 12 month |
| Mechanical properties | Test Condition | Test Method | Chang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PMC T 385J |
|---|---|---|---|
| bending strength | JISK7203 | 95.0 MPa | |
| tensile strength | ASTM D638 | 56.0 MPa | |
| compressive strength | ASTM D695 | 210 MPa | |
| tensile strength | JISK6911 | 56.0 MPa | |
| compression stress | JISK6911 | 210 MPa | |
| bending strength | ASTM D790 | 95.0 MPa |
| Electrical performance | Test Condition | Test Method | Chang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PMC T 385J |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+12 ohms·cm | |
| insulation resistance | --2 | ASTM D257 | 1E+10 ohms |
| dielectric strength | -- | JISK6915 | 10 kV/mm |
| Volume resistivity | JISK6911 | 1E+12 ohms·cm | |
| arc resistance | ASTM D495 | PLC7 | |
| insulation resistance | --3 | ASTM D257 | 1E+08 ohms |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| insulation resistance | --2 | JISK6915 | 1E+10 ohms |
| --3 | JISK6915 | 1E+08 ohms | |
| dielectric strength | -- | ASTM D149 | 10 kV/mm |
| flammability | Test Condition | Test Method | Chang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PMC T 385J |
|---|---|---|---|
| UL flame retardant rating | 6.0mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | Chang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PMC T 385J |
|---|---|---|---|
| Water absorption rate | 24hr | ASTM D570 | 0.30 % |
| density | JISK7112 | 1.42 g/cm³ | |
| Water absorption rate | 23°C,24hr | JISK6911 | 0.30 % |
| Shrinkage rate | -- | JISK6915 | 1.3 % |
| density | ASTM D792 | 1.42 g/cm³ | |
| Shrinkage rate | -- | ASTM D955 | 1.3 % |
| Thermal performance | Test Condition | Test Method | Chang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PMC T 385J |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 160 °C |
| 1.8MPa,未退火，HDT | JISK7207 | 160 °C | |
| RTI Imp | UL 746 | 150 °C | |
| RTI Str | UL 746 | 150 °C | |
| RTI Elec | UL 746 | 150 °C |