PP Homopolymer Niplene T40 Soredi S.p.a.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Soredi S.p.a./Niplene T40 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 30 J/m |
| hardness | Test Condition | Test Method | Soredi S.p.a./Niplene T40 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 106 |
| Mechanical properties | Test Condition | Test Method | Soredi S.p.a./Niplene T40 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 20 % |
| Flexural modulus | ASTM D790 | 4000 MPa | |
| bending strength | 断裂 | ASTM D790 | 50.0 MPa |
| tensile strength | 屈服 | ASTM D638 | 30.0 MPa |
| Electrical performance | Test Condition | Test Method | Soredi S.p.a./Niplene T40 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| dielectric strength | 1.00mm | IEC 60243-1 | 60 kV/mm |
| relative permittivity | 1MHz | IEC 60250 | 2.70 |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.0 |
| flammability | Test Condition | Test Method | Soredi S.p.a./Niplene T40 |
|---|---|---|---|
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 650 °C |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Soredi S.p.a./Niplene T40 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.40to0.80 % |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 8.0 g/10min |
| density | ASTM D792 | 1.24 g/cm³ |
| Thermal performance | Test Condition | Test Method | Soredi S.p.a./Niplene T40 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 90.0 °C |
| vicat | ASTM D15254 | 108 °C |