Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 MKD1016-FW9153 LOTTE KOREA
INFINO®
Electronic and electrical accessories
Glass fiber reinforced,Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LOTTE KOREA/MKD1016-FW9153 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 17 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 17 kJ/m² |
| hardness | Test Condition | Test Method | LOTTE KOREA/MKD1016-FW9153 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 121 |
| R级 | ASTM D785 | 121 |
| Mechanical properties | Test Condition | Test Method | LOTTE KOREA/MKD1016-FW9153 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/5 | 260 Mpa |
| Tensile modulus | ASTM D638 | 19000 Mpa | |
| elongation | 断裂 | ASTM D638 | 4.2 % |
| Tensile modulus | ISO 527-2/50 | 18600 Mpa | |
| bending strength | ISO 178 | 330 Mpa | |
| Flexural modulus | ISO 178 | 16000 Mpa | |
| bending strength | ASTM D790 | 330 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 4.2 % |
| tensile strength | 断裂 | ASTM D638 | 260 Mpa |
| 屈服 | ASTM D638 | 260 Mpa | |
| Flexural modulus | ASTM D790 | 15000 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 260 Mpa |
| flammability | Test Condition | Test Method | LOTTE KOREA/MKD1016-FW9153 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 0.8mm | UL 94 | HB | |
| 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | LOTTE KOREA/MKD1016-FW9153 |
|---|---|---|---|
| ash content | -- | ASTM D5630 | 55 % |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.20-0.30 % |
| ash content | -- | ISO 3451 | 55 % |
| Shrinkage rate | TD:3.20mm | ISO 2577 | 0.30-0.50 % |
| Water absorption rate | 平衡,23°C | ASTM D570 | 3.9 % |
| 平衡,23°C,50%RH | ISO 62 | 3.9 % | |
| Shrinkage rate | TD：3.20mm | ASTM D955 | 0.30-0.50 % |
| melt mass-flow rate | 275°C/2.16kg | ASTM D1238 | 13 g/10min |
| 275°C/2.16kg | ISO 1133 | 13 g/10min | |
| 300°C/1.2kg | ASTM D1238 | 10 g/10min | |
| 300°C/1.2kg | ISO 1133 | 10 g/10min | |
| Shrinkage rate | MD:3.20mm | ISO 2577 | 0.20-0.30 % |
| Thermal performance | Test Condition | Test Method | LOTTE KOREA/MKD1016-FW9153 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 250 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 250 °C |