PA66 Polimid A 30 GF V0A Poliblend S.p.a.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Poliblend S.p.a./Polimid A 30 GF V0A |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180/A | 7.0 kJ/m² | |
| Suspended wall beam without notch impact strength | ISO 180 | 40 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Poliblend S.p.a./Polimid A 30 GF V0A |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2 | 130 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 2.0 % |
| Tensile modulus | ISO 527-2 | 9500 MPa | |
| Tensile strain | 屈服 | ISO 527-2 | 2.0 % |
| tensile strength | 屈服 | ISO 527-2 | 130 MPa |
| Electrical performance | Test Condition | Test Method | Poliblend S.p.a./Polimid A 30 GF V0A |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 |
| flammability | Test Condition | Test Method | Poliblend S.p.a./Polimid A 30 GF V0A |
|---|---|---|---|
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 800 °C |
| UL flame retardant rating | 3.2mm | UL 94 | V-0 |
| 0.8mm | UL 94 | V-0 | |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | Poliblend S.p.a./Polimid A 30 GF V0A |
|---|---|---|---|
| Shrinkage rate | 0.40to0.60 % | ||
| Water absorption rate | 23°C,24hr | ISO 62 | 0.50 % |
| density | ISO 1183 | 1.60 g/cm³ |
| Thermal performance | Test Condition | Test Method | Poliblend S.p.a./Polimid A 30 GF V0A |
|---|---|---|---|
| Heat distortion temperature | 连续使用温度2，HDT | 100 °C | |
| vicat | ISO 306/A120 | 255 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 256 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 245 °C | |
| ball-indentation hardness | 165°C | IEC 60695-10-2 | 通过 |
| melting temperature | DSC | 260 °C |