PC DX06313I GY6E165 SABIC INNOVATIVE NANSHA
LNP™ THERMOCOMP™
Electrical enclosure,Thin walled components
High impact resistance,enhance,High mobility,Filler: Glass fiber reinf,30%,Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX06313I GY6E165 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 16 kJ/m² |
| 23°C | ISO 180/1A | 17 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 24.0 J |
| -30°C | ASTM D256 | 120 J/m | |
| 23°C,Natural&BlackColors | ASTM D256 | 190 J/m | |
| -30°C | ISO 180/1A | 12 kJ/m² | |
| 23°C,Light&WhiteColors | ASTM D256 | 90 J/m |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX06313I GY6E165 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 2.2E-05 cm/cm/°C |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 136 °C | |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 6.8E-05 cm/cm/°C |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 136 °C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX06313I GY6E165 |
|---|---|---|---|
| fracture | ASTM D638 | 99.0 Mpa | |
| --5 | ISO 178 | 6650 Mpa | |
| fracture | ASTM D638 | 3.6 % | |
| ISO 527-2/5 | 3.5 % | ||
| ISO 527-2/5 | 90.0 Mpa | ||
| 50.0mm span | ASTM D790 | 7000 Mpa | |
| --6 | ISO 178 | 170 Mpa | |
| Yield, 50.0mm span | ASTM D790 | 170 Mpa | |
| --1 | ASTM D638 | 7500 Mpa |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX06313I GY6E165 |
|---|---|---|---|
| Melt volume flow rate | 300°C/5.0kg | ISO 1133 | 32.0 cm3/10min |
| melt mass-flow rate | 300°C/5.0kg | ASTM D1238 | 42 g/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.40 % |
| 平衡,23°C,50%RH | ISO 62 | 0.10 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 4.6 g/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.30-0.50 % |