Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI 1110F 8134 SABIC INNOVATIVE US
ULTEM™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/1110F 8134 |
|---|---|---|---|
| Reverse notch impact | 3.20mm | ASTM D256 | 1900 J/m |
| Dart impact | 23°C | ASTM D3029 | 23.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/1110F 8134 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 3720 Mpa | |
| elongation | 断裂 | ASTM D638 | 70 % |
| tensile strength | 屈服 | ASTM D638 | 110 Mpa |
| bending strength | 屈服,100mm跨距 | ASTM D790 | 165 Mpa |
| Flexural modulus | 100mm跨距 | ASTM D790 | 3720 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/1110F 8134 |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 1 |
| arc resistance | ASTM D495 | PLC 5 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/1110F 8134 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 3.0mm | UL 94 | 5VA |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/1110F 8134 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| melt mass-flow rate | 337°C/6.6kg | ASTM D1238 | 16 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/1110F 8134 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 199 °C |
| RTI Imp | UL 746 | 170 °C | |
| RTI | UL 746 | 170 °C | |
| RTI Elec | UL 746 | 170 °C |