LLDPE LL0209AA Malaysia ETILINAS
--
Film bag
Low gel content, high strength, no smoothing agent and anti adhesion agent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | Malaysia ETILINAS/LL0209AA |
|---|---|---|---|
| melt mass-flow rate | 2.16kg | ISO 1133 | 0.9 g/10min |
| density | ISO 1872/1 | 920 kg/m3 |
| Mechanical properties | Test Condition | Test Method | Malaysia ETILINAS/LL0209AA |
|---|---|---|---|
| Tensile stress | TD，断裂 | ISO 1184 | 31 MPa |
| Dart impact | TD | ISO 7765-1(E) | 400 g |
| Tensile stress | TD | ISO 1184 | 12 MPa |
| elongation at break | TD | ISO 1184 | 850 % |
| Elmendorf tear strength | ISO 6368/2 | 160 g/25microns | |
| elongation at break | MD | ISO 1184 | 650 % |
| Tensile stress | MD，断裂 | ISO 1184 | 40 MPa |
| Dart impact | MD | ISO 7765-1(E) | 160 g |
| Tensile stress | MD | ISO 1184 | 11 MPa |
| optical performance | Test Condition | Test Method | Malaysia ETILINAS/LL0209AA |
|---|---|---|---|
| Haze ratio | ASTM D-1003 | 10 % | |
| gloss | 45º | ASTM D-2457 | 54 % |
| Thermal performance | Test Condition | Test Method | Malaysia ETILINAS/LL0209AA |
|---|---|---|---|
| melting temperature | ISO 3146:Method C | 122 ℃ | |
| vicat | ISO 306 | 100 ℃ |