Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PPO ENG265-8746S NR4N77 SABIC INNOVATIVE US
NORYL™
medical care、Profile、Pipe fittings
Thermal stability、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/ENG265-8746S NR4N77 |
---|---|---|---|
Dart impact | 23°C,TotalEnergy | ASTM D3763 | 39.0 J |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.7 kJ/m² |
23°C | ISO 180/1A | 13 kJ/m² | |
Dart impact | -30°C | ASTM D3029 | 25.8 J |
-40°C | ASTM D3029 | 5.42 J |
hardness | Test Condition | Test Method | SABIC INNOVATIVE US/ENG265-8746S NR4N77 |
---|---|---|---|
Rockwell hardness | R级 | ASTM D785 | 119 |
Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/ENG265-8746S NR4N77 |
---|---|---|---|
bending strength | 屈服,50.0mm跨距4 | ASTM D790 | 89.0 Mpa |
Tensile modulus | ISO 527-2/1 | 2550 Mpa | |
elongation | 屈服 | ASTM D638 | 3.3 % |
Tensile strain | 屈服 | ISO 527-2 | 3.1 % |
Flexural modulus | 50.0mm跨距4 | ASTM D790 | 2550 Mpa |
tensile strength | 断裂 | ASTM D638 | 50.0 Mpa |
断裂 | ISO 527-2 | 50.0 Mpa | |
Tensile modulus | ASTM D638 | 2400 Mpa | |
elongation | 断裂 | ASTM D638 | 28 % |
bending strength | ISO 178 | 95.0 Mpa | |
Tensile strain | 断裂 | ISO 527-2 | 27 % |
Flexural modulus | ISO 178 | 2500 Mpa | |
100mmSpan5 | ASTM D790 | 2450 Mpa | |
tensile strength | 屈服 | ASTM D638 | 56.0 Mpa |
屈服 | ISO 527-2 | 55.0 Mpa | |
bending strength | Yield,100mmSpan5 | ASTM D790 | 88.0 Mpa |
Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/ENG265-8746S NR4N77 |
---|---|---|---|
Dissipation Factor | 50Hz | ASTM D150 | 4E-04 |
High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 4 |
Dissipation Factor | 60Hz | ASTM D150 | 4E-04 |
dielectric constant | 60Hz | ASTM D150 | 2.65 |
50Hz | ASTM D150 | 2.65 | |
dielectric strength | 3.20mm,inOil | ASTM D149 | 20 KV/mm |
High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
arc resistance | ASTM D495 | PLC7 | |
Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
flammability | Test Condition | Test Method | SABIC INNOVATIVE US/ENG265-8746S NR4N77 |
---|---|---|---|
UL flame retardant rating | 1.5mm | UL 94 | HB |
physical property | Test Condition | Test Method | SABIC INNOVATIVE US/ENG265-8746S NR4N77 |
---|---|---|---|
Shrinkage rate | MD:3.20mm | 内部方法 | 0.50-0.70 % |
Water absorption rate | 24hr | ASTM D570 | 0.060 % |
melt mass-flow rate | 280°C/5.0kg | ASTM D1238 | 8.5 g/10min |
Melt volume flow rate | 280°C/5.0kg | ISO 1133 | 8.70 cm3/10min |
Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/ENG265-8746S NR4N77 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,6.40mm,HDT | ASTM D648 | 126 °C |
vicat | -- | ISO 306/B120 | 141 °C |
Linear coefficient of thermal expansion | MD:-40到95°C | ASTME831 | 5.9E-05 cm/cm/°C |
Heat distortion temperature | 0.45MPa,未退火,3.20mm,HDT | ASTM D648 | 132 °C |
vicat | -- | ISO 306/B50 | 137 °C |
Heat distortion temperature | 0.45MPa,未退火,6.40mm,HDT | ASTM D648 | 137 °C |
RTI Imp | UL 746 | 90.0 °C | |
RTI Str | UL 746 | 105 °C | |
Heat distortion temperature | 1.8MPa,未退火,3.20mm,HDT | ASTM D648 | 118 °C |
RTI Elec | UL 746 | 105 °C |