Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC XHT4141-RD3G066 SABIC INNOVATIVE NANSHA
LEXAN™ 
Casters,Sports Equipment
High mobility,transparent,High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT4141-RD3G066
Ball Pressure Test163 to 167°CIEC 60695-10-2通过
123 to 127°CIEC 60695-10-2通过
Hot deformation temperature0.45 MPa, Unannealed, 3.20 mmASTM D648174 °C
1.8 MPa, Unannealed, 3.20 mmASTM D648165 °C
0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span9ISO 75-2/Bf173 °C
1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9ISO 75-2/Af162 °C
Linear coefficient of thermal expansionAcross Flow : -40°CISO 11359-26.0E-5 cm/cm/°C
Flow : -40 to 40°CASTM E8316.0E-5 cm/cm/°C
Across Flow : -40 to 40°CASTM E8316.0E-5 cm/cm/°C
RTIUL 746150 °C
RTI ElecUL 746150 °C
RTI ImpUL 746130 °C
thermal conductivity25°CASTM C1770.20 W/m/K
Vicat softening temperature--ISO 306/B120181 °C
--ASTM D152510183 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT4141-RD3G066
Bending modulus--5ISO 1782600 Mpa
50.0 mm Span4ASTM D7902600 Mpa
bending strengthYield, 50.0 mm Span4ASTM D790120 Mpa
--5,6ISO 17880.0 Mpa
elongationYieldISO 527-2/507.0 %
Yield3ASTM D6387.0 %
Break3ASTM D63850 %
BreakISO 527-2/5050 %
Tensile modulus--2ASTM D6382730 Mpa
--ISO 527-2/12750 Mpa
tensile strengthYieldISO 527-2/5078.0 Mpa
BreakISO 527-2/5067.0 Mpa
Break3ASTM D63869.0 Mpa
Yield3ASTM D63877.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT4141-RD3G066
Dielectric constant1 MHzASTM D1503.02
100 HzASTM D1503.12
High arc combustion indexUL 746PLC 0
Hot wire ignitionUL 746PLC 3
Surface resistivityASTM D257> 1.0E+17 ohms
Volume resistivityASTM D257> 1.0E+17 ohms·cm
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT4141-RD3G066
melt mass-flow rate330°C/2.16 kgASTM D123825 g/10 min
Melt Volume Flow Rate (MVR)330°C/2.16 kgISO 113324.0 cm3/10min
Shrinkage rate3.20 mm，FlowInternal Method0.60 - 0.95 %
Water absorption rateSaturation, 23°CISO 620.50 %
Equilibrium, 23°C, 50% RHISO 620.25 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT4141-RD3G066
Charpy Notched Impact Strength23°CISO 179/1eA11 kJ/m²
-30°CISO 179/1eA9.0 kJ/m²
Dart impact23°C, Total EnergyASTM D376372.0 J
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
23°CISO 180/1U无断裂
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT4141-RD3G066
Burning wire flammability index3.0 mmIEC 60695-2-12960 °C
Hot filament ignition temperature3.0 mmIEC 60695-2-13875 °C
Metallic haze起始Internal Method175 °C
UL flame retardant rating3.0 mmUL 94HB
1.5 mmUL 94HB
injectionTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT4141-RD3G066
Back pressure0.300 to 0.700 Mpa
drying temperature135 °C
drying time4.0 to 6.0 hr
Exhaust hole depth0.025 to 0.080 mm
Mold temperature95 to 130 °C
Processing (melt) temperature300 to 345 °C
Screw speed40 to 90 rpm
Spray nozzle temperature295 to 340 °C
Suggested injection volume40 to 60 %
Suggested maximum moisture content0.020 %
Temperature at the front of the material cylinder300 to 345 °C
Temperature at the rear of the barrel280 to 325 °C
Temperature in the middle of the barrel290 to 335 °C