Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI 1000-7101 SABIC INNOVATIVE US
ULTEM™
Automotive sector、Electrical field、Electronic field
Glass fiber reinforced、Flame retardant、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/1000-7101 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 1300 J/m |
| Reverse notch impact | 3.20 mm | ASTM D256 | 1300 J/m |
| Dart impact | 23°C | ASTM D3029 | 36.0 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/1000-7101 |
|---|---|---|---|
| Rockwell hardness | M 级 | ASTM D785 | 109 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/1000-7101 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 3580 Mpa | |
| elongation | 断裂 | ASTM D638 | 60 % |
| 屈服 | ASTM D638 | 7.0 % | |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 转轮 | ASTM D1044 | 10.0 mg |
| bending strength | 屈服, 100 mm 跨距 | ASTM D790 | 165 Mpa |
| tensile strength | 屈服 | ASTM D638 | 110 Mpa |
| Flexural modulus | 100 mm 跨距 | ASTM D790 | 3510 Mpa |
| Poisson's ratio | ASTM E132 | 0.36 |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/1000-7101 |
|---|---|---|---|
| dielectric strength | 1.60 mm, in Oil | ASTM D149 | 28 KV/mm |
| Volume resistivity | ASTM D257 | 1.0E+17 ohms·cm | |
| dielectric constant | 100 Hz | ASTM D150 | 3.15 |
| 1 kHz | ASTM D150 | 3.15 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 4 | |
| High arc combustion index (HAI) | UL 746 | PLC 3 | |
| Dissipation Factor | 1 kHz | ASTM D150 | 1.2E-3 |
| dielectric strength | 3.20 mm, in Oil | ASTM D149 | 20 KV/mm |
| Dissipation Factor | 100 Hz | ASTM D150 | 1.5E-3 |
| 2.45 GHz | ASTM D150 | 2.5E-3 | |
| dielectric strength | 1.60 mm, in Air | ASTM D149 | 33 KV/mm |
| Hot wire ignition (HWI) | UL 746 | PLC 1 | |
| arc resistance | ASTM D495 | PLC 5 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 2 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/1000-7101 |
|---|---|---|---|
| UL flame retardant rating | 3.0 mm | UL 94 | 5VA |
| 0.75 mm | UL 94 | V-0 | |
| 0.40 mm | UL 94 | V-2 | |
| Limiting Oxygen Index | ASTM D2863 | 47 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/1000-7101 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C | ASTM D570 | 1.3 % |
| 24 hr | ASTM D570 | 0.25 % | |
| melt mass-flow rate | 337°C/6.6 kg | ASTM D1238 | 9.0 g/10 min |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/1000-7101 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -20 到 150°C | ASTM E831 | 5.6E-5 cm/cm/°C |
| vicat | ASTM D15254 | 218 °C | |
| thermal conductivity | ASTM C177 | 0.22 W/m/K | |
| Linear coefficient of thermal expansion | 横向 : -20 到 150°C | ASTM E831 | 5.4E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 201 °C |
| RTI Imp | UL 746 | 170 °C | |
| RTI | UL 746 | 170 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 210 °C |
| RTI Elec | UL 746 | 170 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/1000-7101 |
|---|---|---|---|
| screw speed | 40 to 70 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 350 to 400 °C | ||
| drying temperature | 150 °C | ||
| Suggested injection volume | 40 to 60 % | ||
| drying time | 4.0 to 6.0 hr | ||
| Temperature in the middle of the barrel | 340 to 400 °C | ||
| Temperature at the rear of the barrel | 330 to 400 °C | ||
| Exhaust hole depth | 0.025 to 0.076 mm | ||
| Temperature at the front of the material cylinder | 345 to 400 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 135 to 165 °C | ||
| Spray nozzle temperature | 345 to 400 °C |