Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 920A-61009 SABIC INNOVATIVE JAPAN
LEXAN™
Plastic bag、Lighting applications
transparent、wear resistant、UV resistance、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/920A-61009 |
|---|---|---|---|
| Falling hammer impact | 23°C | ASTMD3029 | 169 J |
| Tensile impact strength 4 | ASTMD1822 | 525 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/920A-61009 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ASTMD785 | 118 |
| M计秤 | ASTMD785 | 70 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/920A-61009 |
|---|---|---|---|
| elongation | 屈服 | ASTMD638 | 7.0 % |
| 断裂 | ASTMD638 | 90 % | |
| tensile strength | 屈服 | ASTMD638 | 62.1 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTMD790 | 91.0 Mpa |
| tensile strength | 断裂 | ASTMD638 | 55.8 Mpa |
| 1000Cycles,1000g,CS-17转轮 | ASTMD1044 | 10.0 mg | |
| Flexural modulus | 50.0mm跨距 | ASTMD790 | 2240 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/920A-61009 |
|---|---|---|---|
| Volume resistivity | ASTMD257 | >1.0E+17 ohms·cm | |
| dielectric constant | 1MHz | ASTMD150 | 2.96 |
| 50Hz | ASTMD150 | 3.01 | |
| Dissipation Factor | 60Hz | ASTMD150 | 9E-04 |
| 50Hz | ASTMD150 | 9E-04 | |
| 1MHz | ASTMD150 | 0.010 | |
| Arc resistance 6 | ASTMD495 | PLC7 | |
| dielectric constant | 60Hz | ASTMD150 | 3.01 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL746 | PLC 3 |
| High arc combustion index (HAI) | HAI | UL746 | PLC 3 |
| dielectric strength | 3.20mm,inAir | ASTMD149 | 17 KV/mm |
| Hot wire ignition (HWI) | HWI | UL746 | PLC 2 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL746 | PLC 2 |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/920A-61009 |
|---|---|---|---|
| refractive index | ASTMD542 | 1.586 | |
| transmissivity | 2540µm | ASTMD1003 | 85.0 % |
| Haze ratio | 2540µm | ASTMD1003 | 1.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/920A-61009 |
|---|---|---|---|
| UL flame retardant rating | RadiantPanelListing(UL) | UL94 | YES |
| 3.0mm | UL94 | V-0 | |
| 1.5mm | UL94 | V-2 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/920A-61009 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Water absorption rate | 平衡,23°C | ASTMD570 | 0.35 % |
| melt mass-flow rate | 300°C/1.2kg | ASTMD1238 | 15 g/10min |
| Water absorption rate | 24hr | ASTMD570 | 0.15 % |
| 平衡,100°C | ASTMD570 | 0.58 % | |
| Specific volume | ASTMD792 | 0.835 cm³/g |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/920A-61009 |
|---|---|---|---|
| vicat | ASTMD15255 | 152 °C | |
| MD：-40到95°C | ASTME831 | 6.8E-05 cm/cm/°C | |
| thermal conductivity | ASTMC177 | 0.19 W/m/K | |
| RTI Str | UL746 | 130 °C | |
| RTI Elec | UL746 | 130 °C | |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 132 °C | |
| RTI Imp | UL746 | 120 °C | |
| 0.45MPa,未退火,6.40mm | ASTMD648 | 138 °C |