PC/PBT 1103 BK1066 SABIC INNOVATIVE US
XENOY™
Casters、Plastic bag、Application in the automo
Glass fiber reinforced、Low warpage
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/1103 BK1066 |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 61.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/1103 BK1066 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 1900 Mpa | |
| elongation | 断裂 | ASTM D638 | 150 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 77.2 Mpa |
| elongation | 屈服 | ASTM D638 | 5.0 % |
| tensile strength | 断裂 | ASTM D638 | 50.3 Mpa |
| 屈服 | ASTM D638 | 51.7 Mpa | |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 1930 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/1103 BK1066 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.80-1.0 % |
| melt mass-flow rate | 250°C/5.0kg | ASTM D1238 | 13 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/1103 BK1066 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 2E-04 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 104 °C |
| vicat | ASTM D15255 | 126 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 1.7E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 87.8 °C |