Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LC1700 IDEMITSU JAPAN
TARFLON™
LCD,application
UV resistance,High mobility,Aging resistance,optical performance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/LC1700 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 40 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 90 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2.3(GPa) kg/cm²(MPa)[Lb/in²] | |
| bending strength | ISO 178 | 90 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 40 kJ/m² | |
| Flexural modulus | ISO 178 | 2300 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 65 Mpa |
| elongation at break | ASTM D638/ISO 527 | tB 80 % | |
| ISO 527-2 | 95 % | ||
| tensile strength | ASTM D638/ISO 527 | Y 65 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | IDEMITSU JAPAN/LC1700 |
|---|---|---|---|
| characteristic | 高流动.导光性 |
| Physical properties | Test Condition | Test Method | IDEMITSU JAPAN/LC1700 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.5-0.7 % | |
| density | ASTM D792/ISO 1183 | 1.2 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 40 cm3/10min(300℃/1.2kg ) g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.23 % |
| physical property | Test Condition | Test Method | IDEMITSU JAPAN/LC1700 |
|---|---|---|---|
| Melt volume flow rate | MVR | ISO 1133 | 40 cm3/10min |
| Shrinkage rate | MD: 2.00 mm | 内部方法 | 0.5-0.7 % |
| TD | 内部方法 | 0.5-0.7 % | |
| Water absorption rate | 平衡,23℃, 50% RH | ISO 62 | 0.23 % |
| Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/LC1700 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-2/0.4mm | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 129 ℃（℉） |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 128 °C | |
| UL flame retardant rating | 0.400 mm | UL 94 | V-2 |