PC/ABS TMB1412 MITSUBISHI ENGINEERING JAPAN
IUPILON™
--
--
TDS
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/TMB1412 |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 89.0 °C |
| 1.8MPa,未退火 | ISO75-2/A | 79.0 °C |
| Mechanical Properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/TMB1412 |
|---|---|---|---|
| Flexural Modulus | ISO178 | 4200 Mpa | |
| Tensile Strain | 屈服 | ISO527-2 | 2.6 % |
| Tensile Stress | 屈服 | ISO527-2 | 58.0 Mpa |
| Nominal Tensile Strain at Break | ISO527-2 | 10 % | |
| Flexural Stress | ISO178 | 100 Mpa | |
| Tensile Modulus | ISO527-2 | 4100 Mpa |
| Physical | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/TMB1412 |
|---|---|---|---|
| Melt Volume flow Rate | 260°C/2.16kg | ISO1133 | 20.0 cm3/10min |
| Melt Mass-Flow Rate | 260°C/2.16kg | ISO1133 | 21 g/10min |
| Modeling Shrinkage | TD:3.20mm | 0.15to0.35 % | |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.20 % |
| Modeling Shrinkage | MD:3.20mm | 0.15to0.35 % |
| Impact Properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/TMB1412 |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | 150 kJ/m² |
| Flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/TMB1412 |
|---|---|---|---|
| Flame Rating | 1.0mm | UL94 | V-0 |